Materials Data on Li2V3TeO8 by Materials Project

Abstract

Li2V3TeO8 is Hausmannite-derived structured and crystallizes in the triclinic P1 space group. The structure is three-dimensional. there are eight inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded to six O2- atoms to form LiO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, and edges with six VO6 octahedra. There are a spread of Li–O bond distances ranging from 2.10–2.35 Å. In the second Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three LiO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 44–69°. There are a spread of Li–O bond distances ranging from 2.01–2.12 Å. In the third Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three LiO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 44–71°. There are a spread of Li–O bond distances ranging from 2.00–2.13 Å. In the fourth Li1+ site, Li1+ is bonded to six O2- atoms to form LiO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, and edges with six VO6 octahedra. There are a spread of Li–O bond distances ranging from 2.08–2.34 Å. In the fifth Li1+ site, Li1+ is bonded to six O2- atoms to form LiO6 octahedra that share corners with three LiO4 tetrahedra and edges with six VO6 octahedra. There are a spread of Li–O bond distances ranging from 2.09–2.33 Å. In the sixth Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three LiO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 48–70°. There are a spread of Li–O bond distances ranging from 2.04–2.10 Å. In the seventh Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three LiO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 45–69°. There are a spread of Li–O bond distances ranging from 2.01–2.12 Å. In the eighth Li1+ site, Li1+ is bonded to six O2- atoms to form LiO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, and edges with six VO6 octahedra. There are a spread of Li–O bond distances ranging from 2.07–2.35 Å. There are twelve inequivalent V5+ sites. In the first V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.93–2.29 Å. In the second V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.86–2.35 Å. In the third V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.81–2.46 Å. In the fourth V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.84–2.46 Å. In the fifth V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.95–2.28 Å. In the sixth V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.93–2.30 Å. In the seventh V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.93–2.33 Å. In the eighth V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.95–2.27 Å. In the ninth V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.84–2.47 Å. In the tenth V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.94–2.40 Å. In the eleventh V5+ site, V5+ is bonded to six O2- atoms to form VO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.97–2.26 Å. In the twelfth V5+ site, V5+ is bonded to six O2- atoms to form distorted VO6 octahedra that share a cornercorner with one TeO4 tetrahedra, corners with three LiO4 tetrahedra, edges with two LiO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.92–2.34 Å. There are four inequivalent Te1- sites. In the first Te1- site, Te1- is bonded in a 4-coordinate geometry to four O2- atoms. There are a spread of Te–O bond distances ranging from 1.92–2.63 Å. In the second Te1- site, Te1- is bonded in a 4-coordinate geometry to four O2- atoms. There are a spread of Te–O bond distances ranging from 1.92–2.61 Å. In the third Te1- site, Te1- is bonded in a 4-coordinate geometry to four O2- atoms. There are a spread of Te–O bond distances ranging from 1.91–2.61 Å. In the fourth Te1- site, Te1- is bonded to four O2- atoms to form distorted TeO4 tetrahedra that share corners with three LiO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 52–74°. There are a spread of Te–O bond distances ranging from 1.93–2.56 Å. There are thirty-two inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to two Li1+ and two V5+ atoms. In the second O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to two Li1+ and two V5+ atoms. In the third O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V5+ atoms. In the fourth O2- site, O2- is bonded to two Li1+ and two V5+ atoms to form distorted corner-sharing OLi2V2 trigonal pyramids. In the fifth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the sixth O2- site, O2- is bonded to three V5+ and one Te1- atom to form distorted corner-sharing OV3Te tetrahedra. In the seventh O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the eighth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the ninth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the tenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the eleventh O2- site, O2- is bonded to three V5+ and one Te1- atom to form distorted corner-sharing OV3Te tetrahedra. In the twelfth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the thirteenth O2- site, O2- is bonded to two Li1+ and two V5+ atoms to form distorted corner-sharing OLi2V2 trigonal pyramids. In the fourteenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V5+ atoms. In the fifteenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to two Li1+ and two V5+ atoms. In the sixteenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to two Li1+ and two V5+ atoms. In the seventeenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to two Li1+ and two V5+ atoms. In the eighteenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to two Li1+ and two V5+ atoms. In the nineteenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V5+ atoms. In the twentieth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to two Li1+ and two V5+ atoms. In the twenty-first O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the twenty-second O2- site, O2- is bonded in a distorted tetrahedral geometry to three V5+ and one Te1- atom. In the twenty-third O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the twenty-fourth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the twenty-fifth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the twenty-sixth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the twenty-seventh O2- site, O2- is bonded in a distorted tetrahedral geometry to three V5+ and one Te1- atom. In the twenty-eighth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V5+, and one Te1- atom. In the twenty-ninth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to two Li1+ and two V5+ atoms. In the thirtieth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V5+ atoms. In the thirty-first O2- site, O2- is bonded in a rectangular see-saw-like geometry to two Li1+ and two V5+ atoms. In the thirty-second O2- site, O2- is bonded in a rectangular see-saw-like geometry to two Li1+ and two V5+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Li2V3TeO8 by Materials Project. https://doi.org/10.17188/1303129

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗