Materials Data on Li4Mn3F10 by Materials Project

Abstract

Li4Mn3F10 crystallizes in the monoclinic C2/c space group. The structure is three-dimensional. there are three inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded to five F1- atoms to form distorted LiF5 trigonal bipyramids that share a cornercorner with one LiF4 tetrahedra, corners with two equivalent MnF4 tetrahedra, corners with three equivalent MnF5 trigonal bipyramids, and edges with two equivalent LiF5 trigonal bipyramids. There are a spread of Li–F bond distances ranging from 1.93–2.42 Å. In the second Li1+ site, Li1+ is bonded in a 4-coordinate geometry to four F1- atoms. There is two shorter (1.93 Å) and two longer (1.97 Å) Li–F bond length. In the third Li1+ site, Li1+ is bonded to four F1- atoms to form LiF4 tetrahedra that share corners with two equivalent LiF5 trigonal bipyramids and corners with six equivalent MnF5 trigonal bipyramids. There is two shorter (1.88 Å) and two longer (1.95 Å) Li–F bond length. There are two inequivalent Mn2+ sites. In the first Mn2+ site, Mn2+ is bonded to five F1- atoms to form MnF5 trigonal bipyramids that share a cornercorner with one MnF4 tetrahedra, corners with three equivalent LiF4 tetrahedra, corners with two equivalent MnF5 trigonal bipyramids, and corners with three equivalent LiF5 trigonal bipyramids. There are a spread of Mn–F bond distances ranging from 2.06–2.15 Å. In the second Mn2+ site, Mn2+ is bonded to four F1- atoms to form MnF4 tetrahedra that share corners with two equivalent MnF5 trigonal bipyramids and corners with four equivalent LiF5 trigonal bipyramids. There are two shorter (2.00 Å) and two longer (2.03 Å) Mn–F bond lengths. There are five inequivalent F1- sites. In the first F1- site, F1- is bonded to three Li1+ and one Mn2+ atom to form distorted corner-sharing FLi3Mn tetrahedra. In the second F1- site, F1- is bonded in a distorted trigonal planar geometry to one Li1+ and two equivalent Mn2+ atoms. In the third F1- site, F1- is bonded in a distorted rectangular see-saw-like geometry to three Li1+ and one Mn2+ atom. In the fourth F1- site, F1- is bonded in a 3-coordinate geometry to two equivalent Li1+ and one Mn2+ atom. In the fifth F1- site, F1- is bonded in a bent 120 degrees geometry to two Mn2+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-14. Materials Data on Li4Mn3F10 by Materials Project. https://doi.org/10.17188/1305709

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗