Materials Data on Li2CuPO4 by Materials Project

Abstract

Li2CuPO4 is beta beryllia-derived structured and crystallizes in the triclinic P1 space group. The structure is three-dimensional. there are eight inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with four LiO4 tetrahedra, corners with four CuO4 tetrahedra, and corners with four PO4 tetrahedra. There are a spread of Li–O bond distances ranging from 2.00–2.09 Å. In the second Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with two CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with six LiO4 tetrahedra. There are a spread of Li–O bond distances ranging from 2.00–2.09 Å. In the third Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with four LiO4 tetrahedra, corners with four CuO4 tetrahedra, and corners with four PO4 tetrahedra. There are a spread of Li–O bond distances ranging from 1.94–2.03 Å. In the fourth Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with two equivalent CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with six LiO4 tetrahedra. There are a spread of Li–O bond distances ranging from 1.95–1.99 Å. In the fifth Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share a cornercorner with one CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with seven LiO4 tetrahedra. There are a spread of Li–O bond distances ranging from 1.97–2.03 Å. In the sixth Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with five LiO4 tetrahedra. There are a spread of Li–O bond distances ranging from 1.96–2.03 Å. In the seventh Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with five LiO4 tetrahedra. There are a spread of Li–O bond distances ranging from 2.00–2.10 Å. In the eighth Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with five LiO4 tetrahedra. There is one shorter (1.98 Å) and three longer (2.01 Å) Li–O bond length. There are four inequivalent Cu1+ sites. In the first Cu1+ site, Cu1+ is bonded to four O2- atoms to form CuO4 tetrahedra that share corners with three CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with five LiO4 tetrahedra. There are a spread of Cu–O bond distances ranging from 2.04–2.26 Å. In the second Cu1+ site, Cu1+ is bonded to four O2- atoms to form CuO4 tetrahedra that share corners with three CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with five LiO4 tetrahedra. There are a spread of Cu–O bond distances ranging from 2.04–2.18 Å. In the third Cu1+ site, Cu1+ is bonded to four O2- atoms to form CuO4 tetrahedra that share corners with three CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with five LiO4 tetrahedra. There are a spread of Cu–O bond distances ranging from 2.07–2.21 Å. In the fourth Cu1+ site, Cu1+ is bonded to four O2- atoms to form CuO4 tetrahedra that share a cornercorner with one CuO4 tetrahedra, corners with four PO4 tetrahedra, and corners with seven LiO4 tetrahedra. There are a spread of Cu–O bond distances ranging from 2.06–2.12 Å. There are four inequivalent P5+ sites. In the first P5+ site, P5+ is bonded to four O2- atoms to form PO4 tetrahedra that share corners with three CuO4 tetrahedra and corners with nine LiO4 tetrahedra. There are a spread of P–O bond distances ranging from 1.55–1.57 Å. In the second P5+ site, P5+ is bonded to four O2- atoms to form PO4 tetrahedra that share corners with five CuO4 tetrahedra and corners with seven LiO4 tetrahedra. There are a spread of P–O bond distances ranging from 1.55–1.57 Å. In the third P5+ site, P5+ is bonded to four O2- atoms to form PO4 tetrahedra that share corners with three CuO4 tetrahedra and corners with nine LiO4 tetrahedra. There is three shorter (1.56 Å) and one longer (1.57 Å) P–O bond length. In the fourth P5+ site, P5+ is bonded to four O2- atoms to form PO4 tetrahedra that share corners with five CuO4 tetrahedra and corners with seven LiO4 tetrahedra. There are a spread of P–O bond distances ranging from 1.55–1.57 Å. There are sixteen inequivalent O2- sites. In the first O2- site, O2- is bonded to two Li1+, one Cu1+, and one P5+ atom to form distorted corner-sharing OLi2CuP tetrahedra. In the second O2- site, O2- is bonded to two Li1+, one Cu1+, and one P5+ atom to form distorted corner-sharing OLi2CuP tetrahedra. In the third O2- site, O2- is bonded to three Li1+ and one P5+ atom to form corner-sharing OLi3P tetrahedra. In the fourth O2- site, O2- is bonded to two Li1+, one Cu1+, and one P5+ atom to form distorted corner-sharing OLi2CuP tetrahedra. In the fifth O2- site, O2- is bonded to two Li1+, one Cu1+, and one P5+ atom to form distorted corner-sharing OLi2CuP tetrahedra. In the sixth O2- site, O2- is bonded to three Li1+ and one P5+ atom to form corner-sharing OLi3P tetrahedra. In the seventh O2- site, O2- is bonded to three Li1+ and one P5+ atom to form corner-sharing OLi3P tetrahedra. In the eighth O2- site, O2- is bonded to three Li1+ and one P5+ atom to form corner-sharing OLi3P tetrahedra. In the ninth O2- site, O2- is bonded to two Li1+, one Cu1+, and one P5+ atom to form distorted corner-sharing OLi2CuP tetrahedra. In the tenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two Cu1+, and one P5+ atom. In the eleventh O2- site, O2- is bonded to one Li1+, two Cu1+, and one P5+ atom to form distorted corner-sharing OLiCu2P tetrahedra. In the twelfth O2- site, O2- is bonded to three Li1+ and one P5+ atom to form distorted OLi3P tetrahedra that share corners with nine OLi3P tetrahedra and corners with two equivalent OLi2CuP trigonal pyramids. In the thirteenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two Cu1+, and one P5+ atom. In the fourteenth O2- site, O2- is bonded to two Li1+, one Cu1+, and one P5+ atom to form distorted corner-sharing OLi2CuP trigonal pyramids. In the fifteenth O2- site, O2- is bonded in a 4-coordinate geometry to one Li1+, two Cu1+, and one P5+ atom. In the sixteenth O2- site, O2- is bonded to one Li1+, two Cu1+, and one P5+ atom to form distorted corner-sharing OLiCu2P tetrahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-01. Materials Data on Li2CuPO4 by Materials Project. https://doi.org/10.17188/1306635

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗