Materials Data on Mg(CuO2)2 by Materials Project

Abstract

MgCu2O4 is Spinel-like structured and crystallizes in the triclinic P1 space group. The structure is three-dimensional. there are six inequivalent Mg2+ sites. In the first Mg2+ site, Mg2+ is bonded to four O2- atoms to form MgO4 tetrahedra that share corners with three MgO6 octahedra and corners with nine CuO6 octahedra. The corner-sharing octahedra tilt angles range from 57–60°. There are a spread of Mg–O bond distances ranging from 1.98–2.03 Å. In the second Mg2+ site, Mg2+ is bonded to six O2- atoms to form MgO6 octahedra that share corners with six CuO4 tetrahedra, edges with two MgO6 octahedra, and edges with four CuO6 octahedra. There are a spread of Mg–O bond distances ranging from 2.05–2.12 Å. In the third Mg2+ site, Mg2+ is bonded to six O2- atoms to form MgO6 octahedra that share corners with two equivalent MgO4 tetrahedra, corners with four CuO4 tetrahedra, an edgeedge with one MgO6 octahedra, and edges with five CuO6 octahedra. There are a spread of Mg–O bond distances ranging from 2.04–2.09 Å. In the fourth Mg2+ site, Mg2+ is bonded to six O2- atoms to form MgO6 octahedra that share corners with six CuO4 tetrahedra, edges with two MgO6 octahedra, and edges with four CuO6 octahedra. There are a spread of Mg–O bond distances ranging from 2.05–2.10 Å. In the fifth Mg2+ site, Mg2+ is bonded to six O2- atoms to form MgO6 octahedra that share corners with six CuO4 tetrahedra, edges with two MgO6 octahedra, and edges with four CuO6 octahedra. There are four shorter (2.05 Å) and two longer (2.08 Å) Mg–O bond lengths. In the sixth Mg2+ site, Mg2+ is bonded to six O2- atoms to form MgO6 octahedra that share a cornercorner with one MgO4 tetrahedra, corners with five CuO4 tetrahedra, an edgeedge with one MgO6 octahedra, and edges with five CuO6 octahedra. There are a spread of Mg–O bond distances ranging from 2.05–2.09 Å. There are twelve inequivalent Cu3+ sites. In the first Cu3+ site, Cu3+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with two equivalent MgO4 tetrahedra, corners with four CuO4 tetrahedra, edges with three MgO6 octahedra, and edges with three CuO6 octahedra. There are a spread of Cu–O bond distances ranging from 1.91–2.04 Å. In the second Cu3+ site, Cu3+ is bonded to four O2- atoms to form CuO4 tetrahedra that share corners with six MgO6 octahedra and corners with six CuO6 octahedra. The corner-sharing octahedra tilt angles range from 56–59°. There is two shorter (1.92 Å) and two longer (1.93 Å) Cu–O bond length. In the third Cu3+ site, Cu3+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with three equivalent MgO4 tetrahedra, corners with three equivalent CuO4 tetrahedra, edges with two MgO6 octahedra, and edges with four CuO6 octahedra. There are a spread of Cu–O bond distances ranging from 1.96–2.04 Å. In the fourth Cu3+ site, Cu3+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with two equivalent MgO4 tetrahedra, corners with four CuO4 tetrahedra, edges with three MgO6 octahedra, and edges with three CuO6 octahedra. There are a spread of Cu–O bond distances ranging from 1.91–2.04 Å. In the fifth Cu3+ site, Cu3+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with six CuO4 tetrahedra, edges with two equivalent CuO6 octahedra, and edges with four MgO6 octahedra. There are a spread of Cu–O bond distances ranging from 1.92–2.04 Å. In the sixth Cu3+ site, Cu3+ is bonded to four O2- atoms to form CuO4 tetrahedra that share corners with six MgO6 octahedra and corners with six CuO6 octahedra. The corner-sharing octahedra tilt angles range from 55–60°. There are a spread of Cu–O bond distances ranging from 1.90–1.92 Å. In the seventh Cu3+ site, Cu3+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with six CuO4 tetrahedra, edges with two equivalent CuO6 octahedra, and edges with four MgO6 octahedra. There are a spread of Cu–O bond distances ranging from 1.92–2.04 Å. In the eighth Cu3+ site, Cu3+ is bonded to six O2- atoms to form CuO6 octahedra that share a cornercorner with one MgO4 tetrahedra, corners with five CuO4 tetrahedra, edges with three MgO6 octahedra, and edges with three CuO6 octahedra. There are a spread of Cu–O bond distances ranging from 1.93–2.09 Å. In the ninth Cu3+ site, Cu3+ is bonded to four O2- atoms to form CuO4 tetrahedra that share corners with six MgO6 octahedra and corners with six CuO6 octahedra. The corner-sharing octahedra tilt angles range from 54–61°. There is one shorter (1.91 Å) and three longer (1.93 Å) Cu–O bond length. In the tenth Cu3+ site, Cu3+ is bonded to six O2- atoms to form CuO6 octahedra that share a cornercorner with one MgO4 tetrahedra, corners with five CuO4 tetrahedra, edges with three MgO6 octahedra, and edges with three CuO6 octahedra. There are a spread of Cu–O bond distances ranging from 1.93–2.10 Å. In the eleventh Cu3+ site, Cu3+ is bonded to four O2- atoms to form CuO4 tetrahedra that share corners with six MgO6 octahedra and corners with six CuO6 octahedra. The corner-sharing octahedra tilt angles range from 56–60°. There are a spread of Cu–O bond distances ranging from 1.92–1.99 Å. In the twelfth Cu3+ site, Cu3+ is bonded to four O2- atoms to form CuO4 tetrahedra that share corners with three MgO6 octahedra and corners with nine CuO6 octahedra. The corner-sharing octahedra tilt angles range from 55–62°. There are a spread of Cu–O bond distances ranging from 1.90–1.98 Å. There are twenty-four inequivalent O2- sites. In the first O2- site, O2- is bonded to two Mg2+ and two Cu3+ atoms to form a mixture of distorted edge and corner-sharing OMg2Cu2 trigonal pyramids. In the second O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the third O2- site, O2- is bonded to two Mg2+ and two Cu3+ atoms to form a mixture of distorted edge and corner-sharing OMg2Cu2 trigonal pyramids. In the fourth O2- site, O2- is bonded to one Mg2+ and three Cu3+ atoms to form a mixture of distorted edge and corner-sharing OMgCu3 trigonal pyramids. In the fifth O2- site, O2- is bonded to two Mg2+ and two Cu3+ atoms to form a mixture of distorted edge and corner-sharing OMg2Cu2 trigonal pyramids. In the sixth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the seventh O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the eighth O2- site, O2- is bonded in a rectangular see-saw-like geometry to two Mg2+ and two Cu3+ atoms. In the ninth O2- site, O2- is bonded to two Mg2+ and two Cu3+ atoms to form a mixture of distorted edge and corner-sharing OMg2Cu2 trigonal pyramids. In the tenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the eleventh O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the twelfth O2- site, O2- is bonded in a rectangular see-saw-like geometry to two Mg2+ and two Cu3+ atoms. In the thirteenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to two Mg2+ and two Cu3+ atoms. In the fourteenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the fifteenth O2- site, O2- is bonded to two Mg2+ and two Cu3+ atoms to form a mixture of distorted edge and corner-sharing OMg2Cu2 trigonal pyramids. In the sixteenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to two Mg2+ and two Cu3+ atoms. In the seventeenth O2- site, O2- is bonded to two Mg2+ and two Cu3+ atoms to form distorted corner-sharing OMg2Cu2 trigonal pyramids. In the eighteenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the nineteenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the twentieth O2- site, O2- is bonded to two Mg2+ and two Cu3+ atoms to form a mixture of distorted edge and corner-sharing OMg2Cu2 trigonal pyramids. In the twenty-first O2- site, O2- is bonded in a rectangular see-saw-like geometry to four Cu3+ atoms. In the twenty-second O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the twenty-third O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms. In the twenty-fourth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Mg2+ and three Cu3+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Mg(CuO2)2 by Materials Project. https://doi.org/10.17188/1321288

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗