Alternative High-Performance Ceramic Waste Forms

Abstract

This final report (M5NU-12-NY-AU # 0202-0410) summarizes the results of the project titled “Alternative High-Performance Ceramic Waste Forms,” funded in FY12 by the Nuclear Energy University Program (NEUP Project # 12-3809) being led by Alfred University in collaboration with Savannah River National Laboratory (SRNL). The overall focus of the project is to advance fundamental understanding of crystalline ceramic waste forms and to demonstrate their viability as alternative waste forms to borosilicate glasses. We processed single- and multiphase hollandite waste forms based on simulated waste streams compositions provided by SRNL based on the advanced fuel cycle initiative (AFCI) aqueous separation process developed in the Fuel Cycle Research and Development (FCR&D). For multiphase simulated waste forms, oxide and carbonate precursors were mixed together via ball milling with deionized water using zirconia media in a polyethylene jar for 2 h. The slurry was dried overnight and then separated from the media. The blended powders were then subjected to melting or spark plasma sintering (SPS) processes. Microstructural evolution and phase assemblages of these samples were studied using x-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersion analysis of x-rays (EDAX), wavelength dispersive spectrometry (WDS), transmission electron spectroscopy (TEM), selective area x-ray diffraction (SAXD), and electron backscatter diffraction (EBSD). These results showed that the processing methods have significant effect on the microstructure and thus the performance of these waste forms. The Ce substitution into zirconolite and pyrochlore materials was investigated using a combination of experimental (in situ XRD and x-ray absorption near edge structure (XANES)) and modeling techniques to study these single phases independently. In zirconolite materials, a transition from the 2M to the 4M polymorph was observed with increasing Ce content. The resulting powders were consolidated via SPS. Ce was reduced to the trivalent oxidation state and the zirconolite was converted into undesirable perovskite. The zirconolite polymorphs found in the synthesized powders were recovered after a post-SPS heat treatment in air. These results demonstrated the potential of processing in controlling the phase assemblage in these waste forms. Hollandites with Cr 3+ trivalent cations were identified as potential hosts for Cs immobilization and are being investigated for Cs retention properties. Series of compositions Ba 1.15-x Cs 2x Cr 2.3 Ti 5.7 O 16 , with increasing Cs loadings, were prepared by sol-gel process and characterized for structural parameters. Structural characterization was performed by a combination of powder XRD and neutron powder diffraction. Phase pure hollandite adapting monoclinic symmetry (I2/m) was observed for 0 ≤ x ≤ 0.55. These results were used to develop a new structural model to interpret Cs immobilization in these hollandites. Performance of these waste forms were evaluated for chemical durability and radiation resistance. Product consistency testing (PCT) and vapor hydration testing (VHT) were used for testing of chemical durability. Radiation resistance was tested using He + ions to simulate $\alpha$ particles and heavy ions such as Au 3+ to simulate a recoil. These results showed that these waste forms were chemically durable. The waste forms also amorphized to various degrees on exposure to simulated radiation.