Materials Data on Na4Zn3Se5 by Materials Project

Abstract

Na4Zn3Se5 crystallizes in the orthorhombic Pnma space group. The structure is three-dimensional. there are four inequivalent Na1+ sites. In the first Na1+ site, Na1+ is bonded to five Se2- atoms to form distorted NaSe5 trigonal bipyramids that share corners with two equivalent NaSe6 octahedra, corners with two equivalent NaSe5 square pyramids, corners with three ZnSe4 tetrahedra, corners with four equivalent NaSe5 trigonal bipyramids, an edgeedge with one NaSe6 octahedra, edges with four ZnSe4 tetrahedra, and edges with four NaSe5 trigonal bipyramids. The corner-sharing octahedral tilt angles are 33°. There are a spread of Na–Se bond distances ranging from 2.83–2.94 Å. In the second Na1+ site, Na1+ is bonded to five Se2- atoms to form NaSe5 square pyramids that share corners with three equivalent NaSe6 octahedra, corners with four ZnSe4 tetrahedra, corners with five NaSe5 trigonal bipyramids, edges with four equivalent NaSe5 square pyramids, and edges with four ZnSe4 tetrahedra. The corner-sharing octahedra tilt angles range from 34–54°. There are three shorter (3.08 Å) and two longer (3.13 Å) Na–Se bond lengths. In the third Na1+ site, Na1+ is bonded to six Se2- atoms to form NaSe6 octahedra that share corners with three equivalent NaSe5 square pyramids, corners with five ZnSe4 tetrahedra, corners with four NaSe5 trigonal bipyramids, edges with four equivalent NaSe6 octahedra, edges with five ZnSe4 tetrahedra, an edgeedge with one NaSe5 trigonal bipyramid, and a faceface with one NaSe5 trigonal bipyramid. There are a spread of Na–Se bond distances ranging from 2.99–3.25 Å. In the fourth Na1+ site, Na1+ is bonded to five Se2- atoms to form distorted NaSe5 trigonal bipyramids that share corners with two equivalent NaSe6 octahedra, corners with three equivalent NaSe5 square pyramids, corners with six ZnSe4 tetrahedra, corners with four equivalent NaSe5 trigonal bipyramids, edges with two equivalent ZnSe4 tetrahedra, edges with four NaSe5 trigonal bipyramids, and a faceface with one NaSe6 octahedra. The corner-sharing octahedral tilt angles are 60°. There are a spread of Na–Se bond distances ranging from 2.89–3.07 Å. There are three inequivalent Zn2+ sites. In the first Zn2+ site, Zn2+ is bonded to four Se2- atoms to form ZnSe4 tetrahedra that share a cornercorner with one NaSe6 octahedra, corners with two equivalent NaSe5 square pyramids, corners with six ZnSe4 tetrahedra, corners with three NaSe5 trigonal bipyramids, edges with two equivalent NaSe6 octahedra, and edges with three equivalent NaSe5 square pyramids. The corner-sharing octahedral tilt angles are 15°. There are two shorter (2.52 Å) and two longer (2.53 Å) Zn–Se bond lengths. In the second Zn2+ site, Zn2+ is bonded to four Se2- atoms to form ZnSe4 tetrahedra that share corners with two equivalent NaSe6 octahedra, corners with two equivalent NaSe5 square pyramids, corners with six ZnSe4 tetrahedra, corners with two equivalent NaSe5 trigonal bipyramids, an edgeedge with one NaSe5 square pyramid, and edges with four NaSe5 trigonal bipyramids. The corner-sharing octahedral tilt angles are 48°. There are a spread of Zn–Se bond distances ranging from 2.45–2.61 Å. In the third Zn2+ site, Zn2+ is bonded to four Se2- atoms to form ZnSe4 tetrahedra that share corners with two equivalent NaSe6 octahedra, corners with six ZnSe4 tetrahedra, corners with four equivalent NaSe5 trigonal bipyramids, edges with three equivalent NaSe6 octahedra, and edges with two equivalent NaSe5 trigonal bipyramids. The corner-sharing octahedral tilt angles are 18°. There are a spread of Zn–Se bond distances ranging from 2.48–2.60 Å. There are five inequivalent Se2- sites. In the first Se2- site, Se2- is bonded in a 6-coordinate geometry to four Na1+ and two Zn2+ atoms. In the second Se2- site, Se2- is bonded in a 7-coordinate geometry to five Na1+ and two equivalent Zn2+ atoms. In the third Se2- site, Se2- is bonded in a 8-coordinate geometry to six Na1+ and two Zn2+ atoms. In the fourth Se2- site, Se2- is bonded to three equivalent Na1+ and three Zn2+ atoms to form a mixture of distorted edge and corner-sharing SeNa3Zn3 octahedra. The corner-sharing octahedral tilt angles are 73°. In the fifth Se2- site, Se2- is bonded to three Na1+ and three Zn2+ atoms to form a mixture of distorted edge and corner-sharing SeNa3Zn3 octahedra. The corner-sharing octahedral tilt angles are 73°.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Na4Zn3Se5 by Materials Project. https://doi.org/10.17188/1355011

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗