Materials Data on BaSr7Ti5Mn3O24 by Materials Project

Abstract

BaSr7Ti5Mn3O24 is (Cubic) Perovskite-derived structured and crystallizes in the monoclinic Cm space group. The structure is three-dimensional. Ba2+ is bonded to twelve O2- atoms to form BaO12 cuboctahedra that share corners with twelve SrO12 cuboctahedra, faces with six SrO12 cuboctahedra, faces with three MnO6 octahedra, and faces with five TiO6 octahedra. There are a spread of Ba–O bond distances ranging from 2.81–2.84 Å. There are five inequivalent Sr2+ sites. In the first Sr2+ site, Sr2+ is bonded to twelve O2- atoms to form SrO12 cuboctahedra that share corners with twelve SrO12 cuboctahedra, faces with two equivalent BaO12 cuboctahedra, faces with four SrO12 cuboctahedra, faces with three MnO6 octahedra, and faces with five TiO6 octahedra. There are a spread of Sr–O bond distances ranging from 2.74–2.83 Å. In the second Sr2+ site, Sr2+ is bonded to twelve O2- atoms to form SrO12 cuboctahedra that share corners with four equivalent BaO12 cuboctahedra, corners with eight equivalent SrO12 cuboctahedra, faces with six SrO12 cuboctahedra, faces with three MnO6 octahedra, and faces with five TiO6 octahedra. There are a spread of Sr–O bond distances ranging from 2.72–2.81 Å. In the third Sr2+ site, Sr2+ is bonded to twelve O2- atoms to form SrO12 cuboctahedra that share corners with four equivalent BaO12 cuboctahedra, corners with eight SrO12 cuboctahedra, faces with six SrO12 cuboctahedra, faces with three MnO6 octahedra, and faces with five TiO6 octahedra. There are a spread of Sr–O bond distances ranging from 2.68–2.82 Å. In the fourth Sr2+ site, Sr2+ is bonded to twelve O2- atoms to form SrO12 cuboctahedra that share corners with twelve SrO12 cuboctahedra, faces with six SrO12 cuboctahedra, faces with three MnO6 octahedra, and faces with five TiO6 octahedra. There are a spread of Sr–O bond distances ranging from 2.73–2.80 Å. In the fifth Sr2+ site, Sr2+ is bonded to twelve O2- atoms to form SrO12 cuboctahedra that share corners with twelve SrO12 cuboctahedra, faces with two equivalent BaO12 cuboctahedra, faces with four equivalent SrO12 cuboctahedra, faces with three MnO6 octahedra, and faces with five TiO6 octahedra. There are a spread of Sr–O bond distances ranging from 2.75–2.82 Å. There are four inequivalent Ti4+ sites. In the first Ti4+ site, Ti4+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with two equivalent TiO6 octahedra, corners with four equivalent MnO6 octahedra, a faceface with one BaO12 cuboctahedra, and faces with seven SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–2°. There are a spread of Ti–O bond distances ranging from 1.94–2.01 Å. In the second Ti4+ site, Ti4+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with two equivalent MnO6 octahedra, corners with four equivalent TiO6 octahedra, a faceface with one BaO12 cuboctahedra, and faces with seven SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–2°. There are a spread of Ti–O bond distances ranging from 1.96–1.99 Å. In the third Ti4+ site, Ti4+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with two equivalent MnO6 octahedra, corners with four TiO6 octahedra, a faceface with one BaO12 cuboctahedra, and faces with seven SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–2°. There are a spread of Ti–O bond distances ranging from 1.96–1.99 Å. In the fourth Ti4+ site, Ti4+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with six TiO6 octahedra, a faceface with one BaO12 cuboctahedra, and faces with seven SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–1°. There is three shorter (1.96 Å) and three longer (1.98 Å) Ti–O bond length. There are two inequivalent Mn4+ sites. In the first Mn4+ site, Mn4+ is bonded to six O2- atoms to form MnO6 octahedra that share corners with two equivalent TiO6 octahedra, corners with four equivalent MnO6 octahedra, a faceface with one BaO12 cuboctahedra, and faces with seven SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–3°. There are a spread of Mn–O bond distances ranging from 1.94–1.99 Å. In the second Mn4+ site, Mn4+ is bonded to six O2- atoms to form MnO6 octahedra that share corners with two equivalent MnO6 octahedra, corners with four TiO6 octahedra, a faceface with one BaO12 cuboctahedra, and faces with seven SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–3°. There are a spread of Mn–O bond distances ranging from 1.93–1.97 Å. There are fourteen inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted linear geometry to one Ba2+, three Sr2+, one Ti4+, and one Mn4+ atom. In the second O2- site, O2- is bonded in a distorted linear geometry to one Ba2+, three Sr2+, one Ti4+, and one Mn4+ atom. In the third O2- site, O2- is bonded in a distorted linear geometry to one Ba2+, three Sr2+, and two Ti4+ atoms. In the fourth O2- site, O2- is bonded in a distorted linear geometry to four Sr2+, one Ti4+, and one Mn4+ atom. In the fifth O2- site, O2- is bonded in a distorted linear geometry to four Sr2+, one Ti4+, and one Mn4+ atom. In the sixth O2- site, O2- is bonded in a distorted linear geometry to four Sr2+ and two Ti4+ atoms. In the seventh O2- site, O2- is bonded in a distorted linear geometry to four Sr2+ and two Mn4+ atoms. In the eighth O2- site, O2- is bonded in a distorted linear geometry to four Sr2+, one Ti4+, and one Mn4+ atom. In the ninth O2- site, O2- is bonded in a distorted linear geometry to one Ba2+, three Sr2+, and two Mn4+ atoms. In the tenth O2- site, O2- is bonded in a distorted linear geometry to one Ba2+, three Sr2+, one Ti4+, and one Mn4+ atom. In the eleventh O2- site, O2- is bonded in a distorted linear geometry to four Sr2+ and two Ti4+ atoms. In the twelfth O2- site, O2- is bonded in a distorted linear geometry to four Sr2+ and two Ti4+ atoms. In the thirteenth O2- site, O2- is bonded in a distorted linear geometry to one Ba2+, three Sr2+, and two Ti4+ atoms. In the fourteenth O2- site, O2- is bonded in a distorted linear geometry to one Ba2+, three Sr2+, and two Ti4+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-01. Materials Data on BaSr7Ti5Mn3O24 by Materials Project. https://doi.org/10.17188/1475611

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗