Materials Data on BaSr3Co2(CuO6)2 by Materials Project

Abstract

BaSr3Co2(CuO6)2 is (Cubic) Perovskite-derived structured and crystallizes in the orthorhombic Cmm2 space group. The structure is three-dimensional. Ba is bonded to twelve O atoms to form BaO12 cuboctahedra that share corners with four equivalent BaO12 cuboctahedra, corners with eight equivalent SrO12 cuboctahedra, faces with six SrO12 cuboctahedra, faces with four CoO6 octahedra, and faces with four CuO6 octahedra. There are a spread of Ba–O bond distances ranging from 2.75–2.85 Å. There are three inequivalent Sr sites. In the first Sr site, Sr is bonded to twelve O atoms to form SrO12 cuboctahedra that share corners with twelve SrO12 cuboctahedra, faces with two equivalent BaO12 cuboctahedra, faces with four equivalent SrO12 cuboctahedra, faces with four CoO6 octahedra, and faces with four CuO6 octahedra. There are a spread of Sr–O bond distances ranging from 2.72–2.81 Å. In the second Sr site, Sr is bonded to twelve O atoms to form SrO12 cuboctahedra that share corners with four equivalent SrO12 cuboctahedra, corners with eight equivalent BaO12 cuboctahedra, faces with six SrO12 cuboctahedra, faces with four CoO6 octahedra, and faces with four CuO6 octahedra. There are a spread of Sr–O bond distances ranging from 2.66–2.81 Å. In the third Sr site, Sr is bonded to twelve O atoms to form SrO12 cuboctahedra that share corners with twelve SrO12 cuboctahedra, faces with two equivalent SrO12 cuboctahedra, faces with four equivalent BaO12 cuboctahedra, faces with four CoO6 octahedra, and faces with four CuO6 octahedra. There are a spread of Sr–O bond distances ranging from 2.74–2.83 Å. There are three inequivalent Co sites. In the first Co site, Co is bonded to six O atoms to form CoO6 octahedra that share corners with two equivalent CoO6 octahedra, corners with four CuO6 octahedra, faces with two equivalent BaO12 cuboctahedra, and faces with six SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–2°. There are a spread of Co–O bond distances ranging from 1.90–1.99 Å. In the second Co site, Co is bonded to six O atoms to form CoO6 octahedra that share corners with two equivalent CoO6 octahedra, corners with four equivalent CuO6 octahedra, faces with two equivalent BaO12 cuboctahedra, and faces with six SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–2°. There is one shorter (1.92 Å) and five longer (1.93 Å) Co–O bond length. In the third Co site, Co is bonded to six O atoms to form CoO6 octahedra that share corners with six CoO6 octahedra, faces with two equivalent BaO12 cuboctahedra, and faces with six SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–2°. There are a spread of Co–O bond distances ranging from 1.93–2.04 Å. There are three inequivalent Cu sites. In the first Cu site, Cu is bonded to six O atoms to form CuO6 octahedra that share corners with six CuO6 octahedra, faces with two equivalent BaO12 cuboctahedra, and faces with six SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–4°. There is five shorter (1.97 Å) and one longer (1.98 Å) Cu–O bond length. In the second Cu site, Cu is bonded to six O atoms to form CuO6 octahedra that share corners with two equivalent CuO6 octahedra, corners with four CoO6 octahedra, faces with two equivalent BaO12 cuboctahedra, and faces with six SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–4°. There are a spread of Cu–O bond distances ranging from 1.95–2.02 Å. In the third Cu site, Cu is bonded to six O atoms to form CuO6 octahedra that share corners with two equivalent CuO6 octahedra, corners with four equivalent CoO6 octahedra, faces with two equivalent BaO12 cuboctahedra, and faces with six SrO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–2°. There are a spread of Cu–O bond distances ranging from 1.94–2.01 Å. There are ten inequivalent O sites. In the first O site, O is bonded to one Ba, three Sr, and two Cu atoms to form distorted OBaSr3Cu2 octahedra that share corners with ten OBaSr3Cu2 octahedra, edges with four OBaSr3CoCu octahedra, and faces with seven OBaSr3Cu2 octahedra. The corner-sharing octahedra tilt angles range from 3–62°. In the second O site, O is bonded to one Ba, three Sr, one Co, and one Cu atom to form distorted OBaSr3CoCu octahedra that share corners with sixteen OBaSr3CoCu octahedra, edges with two equivalent OBaSr3Cu2 octahedra, and faces with six OBaSr3Cu2 octahedra. The corner-sharing octahedra tilt angles range from 2–62°. In the third O site, O is bonded to one Ba, three Sr, one Co, and one Cu atom to form distorted OBaSr3CoCu octahedra that share corners with eighteen OBaSr3Cu2 octahedra, edges with two equivalent OBaSr3Cu2 octahedra, and faces with five OBaSr3CoCu octahedra. The corner-sharing octahedra tilt angles range from 1–62°. In the fourth O site, O is bonded in a distorted linear geometry to one Ba, three Sr, and two Co atoms. In the fifth O site, O is bonded to four Sr and two Cu atoms to form distorted OSr4Cu2 octahedra that share corners with ten OBaSr3CoCu octahedra and faces with eight OBaSr3Cu2 octahedra. The corner-sharing octahedra tilt angles range from 0–58°. In the sixth O site, O is bonded in a distorted linear geometry to four Sr, one Co, and one Cu atom. In the seventh O site, O is bonded to two equivalent Ba, two equivalent Sr, and two Cu atoms to form distorted OBa2Sr2Cu2 octahedra that share corners with fourteen OSr4Cu2 octahedra, edges with four equivalent OBa2Sr2CoCu octahedra, and faces with eight OBaSr3Cu2 octahedra. The corner-sharing octahedra tilt angles range from 0–59°. In the eighth O site, O is bonded to two equivalent Ba, two equivalent Sr, one Co, and one Cu atom to form distorted OBa2Sr2CoCu octahedra that share corners with sixteen OBaSr3Cu2 octahedra, edges with four OBa2Sr2Cu2 octahedra, and faces with six OBaSr3Cu2 octahedra. The corner-sharing octahedra tilt angles range from 3–61°. In the ninth O site, O is bonded in a distorted linear geometry to four Sr and two Co atoms. In the tenth O site, O is bonded to two equivalent Ba, two equivalent Sr, and two Co atoms to form distorted OBa2Sr2Co2 octahedra that share corners with twenty OBaSr3Cu2 octahedra, edges with four equivalent OBa2Sr2CoCu octahedra, and faces with four equivalent OBaSr3CoCu octahedra. The corner-sharing octahedra tilt angles range from 0–62°.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-30. Materials Data on BaSr3Co2(CuO6)2 by Materials Project. https://doi.org/10.17188/1476026

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗