Understanding three-dimensionally interconnected porous oxide-derived copper electrocatalyst for selective carbon dioxide reduction

Abstract

In this study, we have investigated a hierarchical CuO-derived inverse opal (CuO-IO) catalyst with high CO selectivity up to 80–90% and minimal H 2 evolution at moderate potentials for CO 2 electroreduction. The three-dimensionally (3D) structured, porous catalyst was composed of small CuO nanoparticles and exhibited a peak CO faradaic efficiency (FE) of 72.5% (±1.8), complete suppression of H 2 formation, and good stability over 24 hours operation at –0.6 V versus the reversible hydrogen electrode (RHE). In situ Raman, X-ray absorption spectroscopy and X-ray diffraction measurements indicated reduction of the catalyst into metallic Cu0 oxidation state with dominant Cu(111) orientation under electrocatalytic conditions. We suggest that rapid depletion of CO 2 and protons at the highly roughened catalyst surface likely increased the local pH during the electrolysis. The combination of C 1 favoring Cu(111) surfaces and reduced local proton/CO 2 availability facilitated selective conversion of CO 2 into CO and reduced H 2 and C 2 products. Our work provides additional understanding of the structure–property relationships of 3D porous electrocatalysts for CO 2 reduction applications by evaluating the crystallographic orientation, oxidation state, and crystallite size of a CO-selective CuO-IO catalyst under realistic working conditions.