Neptunium(IV) Diffusion through Bentonite Clay

Abstract

DOE Fellow, Silvina A. Di Pietro, completed a 10-week internship at Lawrence Livermore National Laboratory (LLNL) in Livermore, California. The objective of the study was to determine the diffusion profile of neptunium (Np) in bentonite clay (potential geo-engineered barrier for nuclear waste repositories). Under the mentorship of Drs. Claudia Joseph (Karlsruhe Institute of Technology, Germany) and Mavrik Zavarin, she prepared a series of core abrasion peeling samples. This procedure was a continuation of a Np diffusion experiment conducted by Dr. Joseph during her post-doc residency at LLNL in the year 2016. The second part of the experiment (from now on will be referred as abrasive peeling) focuses on understanding (1) the Np movement through the clay core and (2) the influence of temperature (25°C, 65°C, and 85°C) for the Np transport across the clay core under anaerobic conditions. End of 2016, the diffusion core samples were embedded in epoxy resin to stabilize them for long-term. The abraded core powder samples vary in material (epoxy vs. clay), Np activity and concentration, temperature exposed during the diffusion experiment, and mass, or amount of clay peeled off. Throughout the course of the 10-week internship program at LLNL, the experiments implemented and discussed in this report aimed to answer the questions: (1) How is the Np(IV) diffusion profile through bentonite influenced by the temperature? and (2) Will Np(IV) migrate through the geoengineered barrier of a nuclear waste repository? In addition, Ph.D. candidate Di Pietro received invaluable guidance in experimental design and development that will benefit her ongoing research endeavors.