Fast-Charging and Ultrahigh-Capacity Lithium Metal Anode Enabled by Surface Alloying

Abstract

Li metal anodes are going through a great revival but they still encounter grand challenges. One often neglected issue is that most reported Li metal anodes are only cyclable under relatively low current density (<5 mA cm -2 ) and small areal capacity (<5 mAh cm -2 ), which essentially limits their high-power applications and results in ineffective Li utilization (<1%). Herein, it is reported that surface alloyed Li metal anodes can enable reversible cycling with ultrafast rate and ultralarge areal capacity. Low-cost Si wafers are used and are chemically etched down to 20-30 mu m membranes. Simply laminating a Si membrane onto Li foil results in the formation of LixSi alloy film fused onto Li metal with mechanical robustness and high Li-ion conductivity. Symmetric cell measurements show that the surface alloyed Li anode has excellent cycling stability, even under high current density up to 25 mA cm -2 and unprecedented areal capacity up to 100 mAh cm -2 . Furthermore, the surface alloyed Li anode is paired with amorphous MoS 3 cathode and achieves remarkable full-cell performance.