Analysis of the sludge batch 9 (Macrobatch 10) DWPF pour stream glass sample

Abstract

A pour stream (PS) sample taken during processing of Sludge Batch 8 (SB8, Macrobatch 10) was analyzed by Savannah River National Laboratory (SRNL) to verify compliance with the Defense Waste Processing Facility (DWPF) Glass Product Control Program. The following conclusions were drawn from these analyses; The sum of oxides for the SB8 PS glass (97.41 wt%) is within the Product Composition Control System (PCCS) limits (100 ± 5 wt%); The average Waste Dilution Factor (WDF) calculated from the Tank 40 dried sludge analysis results for SB8 is 1.9 ± 0.1. In general, the radionuclide concentration of the SB8 PS glass sample calculated using this WDF is in good agreement with the measured radionuclide content; The Product Consistency Test (PCT) results indicate that the SB8 PS glass meets the Waste Acceptance Product Specifications (WAPS) for durability, with normalized release rates for boron, lithium and sodium all at least two standard deviations lower than those of the Environmental Assessment (EA) glass; The average measured density of the SB8 PS glass is 2.72 g/cm 3 , consistent with previous PS samples; and, The average measured Fe 2+ /ΣFe ratio of the SB8 PS glass is 0.15, within the target range of 0.09- 0.33, and closely resembling the predicted REDOX value of 0.15.