Low-temperature bonding with spaced nanorods and eutectic alloys

Stagon, Stephen Peter·Huang, Hanchen·Elliott, Paul Robert
View original source ↗Read source document ↗Export metadata ↓

Abstract

Bonded surfaces are formed by adhering first nanorods and second nanorods to respective first and second surfaces. The first shell is formed on the first nanorods and the second shell is formed on the second nanorods, wherein at least one of the first nanorods and second nanorods, and the first shell and the second shell are formed of distinct metals. The surfaces are then exposed to at least one condition that causes the distinct metals to form an alloy, such as eutectic alloy having a melting point below the temperature at which the alloy is formed, thereby bonding the surfaces upon which solidification of the alloy.

Explore related subjects

36 MATERIALS SCIENCE77 NANOSCIENCE AND NANOTECHNOLOGY

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Stagon, Stephen Peter, Huang, Hanchen, Elliott, Paul Robert. 2020-05-12. Low-temperature bonding with spaced nanorods and eutectic alloys. https://www.osti.gov/biblio/1650879

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗