Materials Data on Li2B3O4F3 by Materials Project

Abstract

Li2B3O4F3 crystallizes in the orthorhombic P2_12_12_1 space group. The structure is three-dimensional. there are two inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded to two O2- and two F1- atoms to form LiO2F2 tetrahedra that share corners with four BO3F tetrahedra. There is one shorter (1.96 Å) and one longer (1.99 Å) Li–O bond length. Both Li–F bond lengths are 1.91 Å. In the second Li1+ site, Li1+ is bonded in a 4-coordinate geometry to three O2- and two F1- atoms. There are a spread of Li–O bond distances ranging from 2.01–2.12 Å. There are one shorter (1.86 Å) and one longer (2.58 Å) Li–F bond lengths. There are three inequivalent B3+ sites. In the first B3+ site, B3+ is bonded to three O2- and one F1- atom to form BO3F tetrahedra that share a cornercorner with one LiO2F2 tetrahedra and a cornercorner with one BO2F2 tetrahedra. All B–O bond lengths are 1.46 Å. The B–F bond length is 1.46 Å. In the second B3+ site, B3+ is bonded to two O2- and two F1- atoms to form BO2F2 tetrahedra that share a cornercorner with one BO3F tetrahedra and corners with three equivalent LiO2F2 tetrahedra. There is one shorter (1.44 Å) and one longer (1.46 Å) B–O bond length. There is one shorter (1.45 Å) and one longer (1.46 Å) B–F bond length. In the third B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. There is one shorter (1.37 Å) and two longer (1.38 Å) B–O bond length. There are four inequivalent O2- sites. In the first O2- site, O2- is bonded in a 3-coordinate geometry to one Li1+ and two B3+ atoms. In the second O2- site, O2- is bonded to two equivalent Li1+ and two B3+ atoms to form distorted corner-sharing OLi2B2 tetrahedra. In the third O2- site, O2- is bonded in a trigonal planar geometry to one Li1+ and two B3+ atoms. In the fourth O2- site, O2- is bonded in a trigonal planar geometry to one Li1+ and two B3+ atoms. There are three inequivalent F1- sites. In the first F1- site, F1- is bonded in a distorted bent 150 degrees geometry to two Li1+ and one B3+ atom. In the second F1- site, F1- is bonded in a bent 150 degrees geometry to one Li1+ and one B3+ atom. In the third F1- site, F1- is bonded in a bent 150 degrees geometry to one Li1+ and one B3+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Li2B3O4F3 by Materials Project. https://doi.org/10.17188/1676249

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗