Materials Data on NbCrNi by Materials Project

Abstract

CrNiNb crystallizes in the orthorhombic Amm2 space group. The structure is three-dimensional. there are seven inequivalent Nb sites. In the first Nb site, Nb is bonded in a 12-coordinate geometry to four Nb, seven Cr, and five Ni atoms. There are one shorter (2.96 Å) and three longer (2.98 Å) Nb–Nb bond lengths. There are a spread of Nb–Cr bond distances ranging from 2.82–2.92 Å. There are a spread of Nb–Ni bond distances ranging from 2.81–2.85 Å. In the second Nb site, Nb is bonded in a 12-coordinate geometry to four Nb, five Cr, and seven Ni atoms. There are one shorter (2.96 Å) and one longer (2.99 Å) Nb–Nb bond lengths. There are a spread of Nb–Cr bond distances ranging from 2.81–2.94 Å. There are a spread of Nb–Ni bond distances ranging from 2.82–2.90 Å. In the third Nb site, Nb is bonded in a 12-coordinate geometry to four Nb, five Cr, and seven Ni atoms. There are one shorter (2.96 Å) and two longer (2.98 Å) Nb–Nb bond lengths. There are a spread of Nb–Cr bond distances ranging from 2.81–2.94 Å. There are a spread of Nb–Ni bond distances ranging from 2.82–2.90 Å. In the fourth Nb site, Nb is bonded in a 12-coordinate geometry to four Nb, seven Cr, and five Ni atoms. The Nb–Nb bond length is 2.96 Å. There are a spread of Nb–Cr bond distances ranging from 2.82–2.92 Å. There are a spread of Nb–Ni bond distances ranging from 2.81–2.85 Å. In the fifth Nb site, Nb is bonded in a 12-coordinate geometry to four Nb, seven Cr, and five Ni atoms. All Nb–Nb bond lengths are 2.98 Å. There are a spread of Nb–Cr bond distances ranging from 2.82–2.92 Å. There are a spread of Nb–Ni bond distances ranging from 2.81–2.85 Å. In the sixth Nb site, Nb is bonded in a 12-coordinate geometry to four Nb, five Cr, and seven Ni atoms. There are two shorter (2.98 Å) and one longer (2.99 Å) Nb–Nb bond lengths. There are a spread of Nb–Cr bond distances ranging from 2.81–2.94 Å. There are a spread of Nb–Ni bond distances ranging from 2.82–2.90 Å. In the seventh Nb site, Nb is bonded in a 12-coordinate geometry to four Nb, seven Cr, and five Ni atoms. There are a spread of Nb–Cr bond distances ranging from 2.82–2.92 Å. There are a spread of Nb–Ni bond distances ranging from 2.81–2.85 Å. There are two inequivalent Cr sites. In the first Cr site, Cr is bonded to six Nb, two equivalent Cr, and four Ni atoms to form distorted CrNb6Cr2Ni4 cuboctahedra that share corners with four equivalent CrNb6Cr4Ni2 cuboctahedra, corners with eight NiNb6Cr6 cuboctahedra, edges with six equivalent CrNb6Cr2Ni4 cuboctahedra, faces with eight CrNb6Cr2Ni4 cuboctahedra, and faces with twelve NiNb6Cr6 cuboctahedra. Both Cr–Cr bond lengths are 2.40 Å. There are a spread of Cr–Ni bond distances ranging from 2.43–2.47 Å. In the second Cr site, Cr is bonded to six Nb, four Cr, and two equivalent Ni atoms to form distorted CrNb6Cr4Ni2 cuboctahedra that share corners with eight CrNb6Cr2Ni4 cuboctahedra, corners with ten NiNb6Cr2Ni4 cuboctahedra, edges with two equivalent CrNb6Cr4Ni2 cuboctahedra, edges with four equivalent NiNb6Cr2Ni4 cuboctahedra, faces with eight NiNb6Cr6 cuboctahedra, and faces with ten CrNb6Cr2Ni4 cuboctahedra. There are one shorter (2.39 Å) and one longer (2.41 Å) Cr–Cr bond lengths. There are one shorter (2.40 Å) and one longer (2.51 Å) Cr–Ni bond lengths. There are three inequivalent Ni sites. In the first Ni site, Ni is bonded to six Nb and six Cr atoms to form NiNb6Cr6 cuboctahedra that share corners with four equivalent CrNb6Cr2Ni4 cuboctahedra, corners with fourteen NiNb6Cr6 cuboctahedra, edges with six NiNb6Cr6 cuboctahedra, faces with four equivalent NiNb6Cr2Ni4 cuboctahedra, and faces with fourteen CrNb6Cr2Ni4 cuboctahedra. In the second Ni site, Ni is bonded to six Nb, two equivalent Cr, and four Ni atoms to form distorted NiNb6Cr2Ni4 cuboctahedra that share corners with eight NiNb6Cr6 cuboctahedra, corners with ten CrNb6Cr2Ni4 cuboctahedra, edges with two equivalent NiNb6Cr2Ni4 cuboctahedra, edges with four equivalent CrNb6Cr4Ni2 cuboctahedra, faces with eight CrNb6Cr2Ni4 cuboctahedra, and faces with ten NiNb6Cr6 cuboctahedra. There are a spread of Ni–Ni bond distances ranging from 2.37–2.48 Å. In the third Ni site, Ni is bonded to six Nb, two equivalent Cr, and four equivalent Ni atoms to form distorted NiNb6Cr2Ni4 cuboctahedra that share corners with six NiNb6Cr6 cuboctahedra, corners with twelve CrNb6Cr2Ni4 cuboctahedra, edges with six NiNb6Cr6 cuboctahedra, faces with eight equivalent NiNb6Cr2Ni4 cuboctahedra, and faces with ten CrNb6Cr2Ni4 cuboctahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-04. Materials Data on NbCrNi by Materials Project. https://doi.org/10.17188/1678449

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗