Materials Data on Li4(AlCu2)3 by Materials Project

Abstract

Li4(Cu2Al)3 is Frank-Kasper $\mu$ Phase-derived structured and crystallizes in the hexagonal P6_3/mmc space group. The structure is three-dimensional. there are four inequivalent Li sites. In the first Li site, Li is bonded in a 1-coordinate geometry to three equivalent Li, nine equivalent Cu, and four Al atoms. All Li–Li bond lengths are 2.93 Å. There are three shorter (2.79 Å) and six longer (2.97 Å) Li–Cu bond lengths. There are one shorter (2.62 Å) and three longer (2.86 Å) Li–Al bond lengths. In the second Li site, Li is bonded in a 1-coordinate geometry to three equivalent Li, nine equivalent Cu, and four Al atoms. There are three shorter (2.79 Å) and six longer (2.97 Å) Li–Cu bond lengths. There are one shorter (2.62 Å) and three longer (2.86 Å) Li–Al bond lengths. In the third Li site, Li is bonded in a 6-coordinate geometry to six equivalent Cu and six Al atoms. All Li–Cu bond lengths are 2.71 Å. All Li–Al bond lengths are 3.15 Å. In the fourth Li site, Li is bonded in a 6-coordinate geometry to six equivalent Cu and six Al atoms. All Li–Cu bond lengths are 2.72 Å. All Li–Al bond lengths are 3.15 Å. Cu is bonded to five Li, four equivalent Cu, and three Al atoms to form CuLi5Al3Cu4 cuboctahedra that share corners with two equivalent AlLi6Cu6 cuboctahedra, corners with thirteen equivalent CuLi5Al3Cu4 cuboctahedra, edges with five equivalent CuLi5Al3Cu4 cuboctahedra, faces with three equivalent AlLi6Cu6 cuboctahedra, and faces with ten equivalent CuLi5Al3Cu4 cuboctahedra. There are two shorter (2.42 Å) and two longer (2.48 Å) Cu–Cu bond lengths. There are one shorter (2.49 Å) and two longer (2.63 Å) Cu–Al bond lengths. There are four inequivalent Al sites. In the first Al site, Al is bonded to six Li and six equivalent Cu atoms to form AlLi6Cu6 cuboctahedra that share corners with twelve equivalent CuLi5Al3Cu4 cuboctahedra, edges with six equivalent AlLi6Cu6 cuboctahedra, and faces with eighteen equivalent CuLi5Al3Cu4 cuboctahedra. In the second Al site, Al is bonded in a 1-coordinate geometry to seven Li, six equivalent Cu, and one Al atom. All Al–Cu bond lengths are 2.63 Å. The Al–Al bond length is 2.74 Å. In the third Al site, Al is bonded in a 1-coordinate geometry to seven Li, six equivalent Cu, and one Al atom. The Al–Li bond length is 2.62 Å. The Al–Al bond length is 2.74 Å. In the fourth Al site, Al is bonded in a 1-coordinate geometry to seven Li, six equivalent Cu, and one Al atom. There are one shorter (2.62 Å) and six longer (3.15 Å) Al–Li bond lengths. All Al–Cu bond lengths are 2.63 Å.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Li4(AlCu2)3 by Materials Project. https://doi.org/10.17188/1679744

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗