Materials Data on La2(CuNi)5 by Materials Project

Abstract

La2(NiCu)5 crystallizes in the orthorhombic Pmmm space group. The structure is three-dimensional. there are two inequivalent La sites. In the first La site, La is bonded in a 6-coordinate geometry to twelve Ni and six Cu atoms. There are eight shorter (3.22 Å) and four longer (3.23 Å) La–Ni bond lengths. There are two shorter (2.92 Å) and four longer (2.95 Å) La–Cu bond lengths. In the second La site, La is bonded in a 6-coordinate geometry to eight equivalent Ni and ten Cu atoms. All La–Ni bond lengths are 3.23 Å. There are a spread of La–Cu bond distances ranging from 2.93–3.23 Å. There are two inequivalent Ni sites. In the first Ni site, Ni is bonded to four equivalent La, four equivalent Ni, and four equivalent Cu atoms to form NiLa4Cu4Ni4 cuboctahedra that share corners with four equivalent CuLa4Cu4Ni4 cuboctahedra, corners with twelve NiLa4Cu5Ni3 cuboctahedra, edges with ten NiLa4Cu5Ni3 cuboctahedra, and faces with ten NiLa4Cu4Ni4 cuboctahedra. All Ni–Ni bond lengths are 2.53 Å. All Ni–Cu bond lengths are 2.47 Å. In the second Ni site, Ni is bonded to four La, three Ni, and five Cu atoms to form NiLa4Cu5Ni3 cuboctahedra that share corners with two equivalent CuLa4Cu4Ni4 cuboctahedra, corners with fourteen NiLa4Cu4Ni4 cuboctahedra, edges with two equivalent CuLa4Cu4Ni4 cuboctahedra, edges with eight NiLa4Cu4Ni4 cuboctahedra, faces with two equivalent CuLa4Cu4Ni4 cuboctahedra, and faces with eight NiLa4Cu4Ni4 cuboctahedra. There are one shorter (2.54 Å) and one longer (2.57 Å) Ni–Ni bond lengths. There are a spread of Ni–Cu bond distances ranging from 2.46–2.56 Å. There are three inequivalent Cu sites. In the first Cu site, Cu is bonded in a 12-coordinate geometry to three La, four equivalent Ni, and two equivalent Cu atoms. Both Cu–Cu bond lengths are 2.48 Å. In the second Cu site, Cu is bonded in a 12-coordinate geometry to three La and six Ni atoms. In the third Cu site, Cu is bonded to four equivalent La, four equivalent Ni, and four equivalent Cu atoms to form CuLa4Cu4Ni4 cuboctahedra that share corners with four equivalent CuLa4Cu4Ni4 cuboctahedra, corners with twelve NiLa4Cu5Ni3 cuboctahedra, edges with two equivalent CuLa4Cu4Ni4 cuboctahedra, edges with eight equivalent NiLa4Cu5Ni3 cuboctahedra, faces with two equivalent CuLa4Cu4Ni4 cuboctahedra, and faces with eight equivalent NiLa4Cu5Ni3 cuboctahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-03. Materials Data on La2(CuNi)5 by Materials Project. https://doi.org/10.17188/1682862

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗