Materials Data on Th2(FeNi)5 by Materials Project

Abstract

Th2(FeNi)5 crystallizes in the orthorhombic Pmmm space group. The structure is three-dimensional. there are two inequivalent Th sites. In the first Th site, Th is bonded in a 6-coordinate geometry to six Fe and twelve Ni atoms. There are four shorter (2.91 Å) and two longer (2.92 Å) Th–Fe bond lengths. There are eight shorter (3.20 Å) and four longer (3.22 Å) Th–Ni bond lengths. In the second Th site, Th is bonded in a 6-coordinate geometry to ten Fe and eight equivalent Ni atoms. There are a spread of Th–Fe bond distances ranging from 2.87–3.22 Å. All Th–Ni bond lengths are 3.20 Å. There are three inequivalent Fe sites. In the first Fe site, Fe is bonded in a 12-coordinate geometry to three Th, two equivalent Fe, and four equivalent Ni atoms. Both Fe–Fe bond lengths are 2.44 Å. All Fe–Ni bond lengths are 2.49 Å. In the second Fe site, Fe is bonded in a 12-coordinate geometry to three Th and six Ni atoms. There are four shorter (2.46 Å) and two longer (2.47 Å) Fe–Ni bond lengths. In the third Fe site, Fe is bonded to four equivalent Th, four equivalent Fe, and four equivalent Ni atoms to form distorted FeTh4Fe4Ni4 cuboctahedra that share corners with four equivalent FeTh4Fe4Ni4 cuboctahedra, corners with twelve NiTh4Fe5Ni3 cuboctahedra, edges with two equivalent FeTh4Fe4Ni4 cuboctahedra, edges with eight equivalent NiTh4Fe5Ni3 cuboctahedra, faces with two equivalent FeTh4Fe4Ni4 cuboctahedra, and faces with eight equivalent NiTh4Fe5Ni3 cuboctahedra. All Fe–Ni bond lengths are 2.51 Å. There are two inequivalent Ni sites. In the first Ni site, Ni is bonded to four equivalent Th, four equivalent Fe, and four equivalent Ni atoms to form distorted NiTh4Fe4Ni4 cuboctahedra that share corners with four equivalent FeTh4Fe4Ni4 cuboctahedra, corners with twelve NiTh4Fe5Ni3 cuboctahedra, edges with ten NiTh4Fe5Ni3 cuboctahedra, and faces with ten NiTh4Fe4Ni4 cuboctahedra. All Ni–Ni bond lengths are 2.49 Å. In the second Ni site, Ni is bonded to four Th, five Fe, and three Ni atoms to form distorted NiTh4Fe5Ni3 cuboctahedra that share corners with two equivalent FeTh4Fe4Ni4 cuboctahedra, corners with fourteen NiTh4Fe4Ni4 cuboctahedra, edges with two equivalent FeTh4Fe4Ni4 cuboctahedra, edges with eight NiTh4Fe4Ni4 cuboctahedra, faces with two equivalent FeTh4Fe4Ni4 cuboctahedra, and faces with eight NiTh4Fe4Ni4 cuboctahedra. There are one shorter (2.50 Å) and one longer (2.54 Å) Ni–Ni bond lengths.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-06-05. Materials Data on Th2(FeNi)5 by Materials Project. https://doi.org/10.17188/1684568

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗