Materials Data on La9In5Se21 by Materials Project

Abstract

La9In5Se21 crystallizes in the trigonal R3 space group. The structure is three-dimensional. there are six inequivalent La3+ sites. In the first La3+ site, La3+ is bonded in a 7-coordinate geometry to seven Se2- atoms. There are a spread of La–Se bond distances ranging from 3.03–3.24 Å. In the second La3+ site, La3+ is bonded in a 8-coordinate geometry to eight Se2- atoms. There are a spread of La–Se bond distances ranging from 3.02–3.50 Å. In the third La3+ site, La3+ is bonded in a 7-coordinate geometry to seven Se2- atoms. There are a spread of La–Se bond distances ranging from 3.02–3.29 Å. In the fourth La3+ site, La3+ is bonded in a 7-coordinate geometry to seven Se2- atoms. There are a spread of La–Se bond distances ranging from 3.00–3.25 Å. In the fifth La3+ site, La3+ is bonded in a 8-coordinate geometry to eight Se2- atoms. There are a spread of La–Se bond distances ranging from 3.02–3.47 Å. In the sixth La3+ site, La3+ is bonded in a 7-coordinate geometry to seven Se2- atoms. There are a spread of La–Se bond distances ranging from 3.02–3.33 Å. There are six inequivalent In3+ sites. In the first In3+ site, In3+ is bonded in a tetrahedral geometry to four Se2- atoms. There are a spread of In–Se bond distances ranging from 2.56–2.62 Å. In the second In3+ site, In3+ is bonded in a tetrahedral geometry to four Se2- atoms. There are a spread of In–Se bond distances ranging from 2.56–2.61 Å. In the third In3+ site, In3+ is bonded to six Se2- atoms to form face-sharing InSe6 octahedra. There are three shorter (2.75 Å) and three longer (2.85 Å) In–Se bond lengths. In the fourth In3+ site, In3+ is bonded to six Se2- atoms to form distorted face-sharing InSe6 octahedra. There are three shorter (2.66 Å) and three longer (3.02 Å) In–Se bond lengths. In the fifth In3+ site, In3+ is bonded to six Se2- atoms to form distorted face-sharing InSe6 octahedra. There are three shorter (2.66 Å) and three longer (3.02 Å) In–Se bond lengths. In the sixth In3+ site, In3+ is bonded to six Se2- atoms to form face-sharing InSe6 octahedra. There are three shorter (2.75 Å) and three longer (2.84 Å) In–Se bond lengths. There are fourteen inequivalent Se2- sites. In the first Se2- site, Se2- is bonded in a 5-coordinate geometry to four La3+ and one In3+ atom. In the second Se2- site, Se2- is bonded to three La3+ and two In3+ atoms to form distorted SeLa3In2 square pyramids that share corners with three SeLa3In tetrahedra, a cornercorner with one SeLa3In trigonal pyramid, edges with two equivalent SeLa3In trigonal pyramids, and faces with two equivalent SeLa3In2 square pyramids. In the third Se2- site, Se2- is bonded to three La3+ and one In3+ atom to form distorted SeLa3In trigonal pyramids that share a cornercorner with one SeLa3In2 square pyramid, corners with three SeLa3In tetrahedra, edges with two equivalent SeLa3In2 square pyramids, and edges with two equivalent SeLa3In trigonal pyramids. In the fourth Se2- site, Se2- is bonded to three La3+ and two In3+ atoms to form distorted SeLa3In2 square pyramids that share corners with three SeLa3In tetrahedra, a cornercorner with one SeLa3In trigonal pyramid, edges with two equivalent SeLa3In trigonal pyramids, and faces with two equivalent SeLa3In2 square pyramids. In the fifth Se2- site, Se2- is bonded to three La3+ and one In3+ atom to form distorted SeLa3In trigonal pyramids that share a cornercorner with one SeLa3In2 square pyramid, corners with three SeLa3In tetrahedra, edges with two equivalent SeLa3In2 square pyramids, and edges with two equivalent SeLa3In trigonal pyramids. In the sixth Se2- site, Se2- is bonded in a 5-coordinate geometry to four La3+ and one In3+ atom. In the seventh Se2- site, Se2- is bonded to three La3+ and one In3+ atom to form SeLa3In tetrahedra that share corners with three SeLa3In2 square pyramids and corners with three SeLa3In trigonal pyramids. In the eighth Se2- site, Se2- is bonded to three La3+ and one In3+ atom to form SeLa3In tetrahedra that share corners with three SeLa3In2 square pyramids and corners with three SeLa3In trigonal pyramids. In the ninth Se2- site, Se2- is bonded in a distorted rectangular see-saw-like geometry to three La3+ and one In3+ atom. In the tenth Se2- site, Se2- is bonded in a distorted rectangular see-saw-like geometry to three La3+ and one In3+ atom. In the eleventh Se2- site, Se2- is bonded in a distorted rectangular see-saw-like geometry to three La3+ and one In3+ atom. In the twelfth Se2- site, Se2- is bonded in a distorted rectangular see-saw-like geometry to three La3+ and one In3+ atom. In the thirteenth Se2- site, Se2- is bonded in a distorted rectangular see-saw-like geometry to three La3+ and one In3+ atom. In the fourteenth Se2- site, Se2- is bonded in a distorted rectangular see-saw-like geometry to three La3+ and one In3+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on La9In5Se21 by Materials Project. https://doi.org/10.17188/1704892

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗