Materials Data on Ba5SrLa2Fe4O15 by Materials Project

Abstract

Ba5SrLa2Fe4O15 crystallizes in the monoclinic Cc space group. The structure is three-dimensional. there are five inequivalent Ba2+ sites. In the first Ba2+ site, Ba2+ is bonded to six O2- atoms to form BaO6 octahedra that share corners with six FeO4 tetrahedra and faces with two equivalent BaO6 octahedra. There are a spread of Ba–O bond distances ranging from 2.59–2.76 Å. In the second Ba2+ site, Ba2+ is bonded in a 10-coordinate geometry to ten O2- atoms. There are a spread of Ba–O bond distances ranging from 2.78–3.30 Å. In the third Ba2+ site, Ba2+ is bonded in a 10-coordinate geometry to ten O2- atoms. There are a spread of Ba–O bond distances ranging from 2.78–3.26 Å. In the fourth Ba2+ site, Ba2+ is bonded in a 10-coordinate geometry to ten O2- atoms. There are a spread of Ba–O bond distances ranging from 2.79–3.28 Å. In the fifth Ba2+ site, Ba2+ is bonded to twelve O2- atoms to form distorted BaO12 cuboctahedra that share faces with two equivalent FeO6 octahedra and faces with three FeO4 tetrahedra. There are a spread of Ba–O bond distances ranging from 2.75–3.28 Å. Sr2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Sr–O bond distances ranging from 2.47–2.80 Å. There are two inequivalent La3+ sites. In the first La3+ site, La3+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of La–O bond distances ranging from 2.40–2.73 Å. In the second La3+ site, La3+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of La–O bond distances ranging from 2.40–2.74 Å. There are four inequivalent Fe3+ sites. In the first Fe3+ site, Fe3+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with three FeO4 tetrahedra and faces with two equivalent BaO12 cuboctahedra. There are a spread of Fe–O bond distances ranging from 1.96–2.21 Å. In the second Fe3+ site, Fe3+ is bonded to four O2- atoms to form FeO4 tetrahedra that share a cornercorner with one FeO6 octahedra, corners with two equivalent BaO6 octahedra, and a faceface with one BaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 5–67°. There are a spread of Fe–O bond distances ranging from 1.87–1.94 Å. In the third Fe3+ site, Fe3+ is bonded to four O2- atoms to form FeO4 tetrahedra that share a cornercorner with one FeO6 octahedra, corners with two equivalent BaO6 octahedra, and a faceface with one BaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 7–67°. There are a spread of Fe–O bond distances ranging from 1.86–1.94 Å. In the fourth Fe3+ site, Fe3+ is bonded to four O2- atoms to form FeO4 tetrahedra that share a cornercorner with one FeO6 octahedra, corners with two equivalent BaO6 octahedra, and a faceface with one BaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 5–67°. There are a spread of Fe–O bond distances ranging from 1.86–1.94 Å. There are fifteen inequivalent O2- sites. In the first O2- site, O2- is bonded in a 6-coordinate geometry to three Ba2+, one Sr2+, one La3+, and one Fe3+ atom. In the second O2- site, O2- is bonded in a 2-coordinate geometry to three Ba2+, two equivalent La3+, and one Fe3+ atom. In the third O2- site, O2- is bonded in a 2-coordinate geometry to three Ba2+, one Sr2+, one La3+, and one Fe3+ atom. In the fourth O2- site, O2- is bonded in a 6-coordinate geometry to three Ba2+, one Sr2+, one La3+, and one Fe3+ atom. In the fifth O2- site, O2- is bonded in a 2-coordinate geometry to three Ba2+, one Sr2+, one La3+, and one Fe3+ atom. In the sixth O2- site, O2- is bonded in a 2-coordinate geometry to three Ba2+, two equivalent La3+, and one Fe3+ atom. In the seventh O2- site, O2- is bonded in a 1-coordinate geometry to five Ba2+ and one Fe3+ atom. In the eighth O2- site, O2- is bonded in a 1-coordinate geometry to five Ba2+ and one Fe3+ atom. In the ninth O2- site, O2- is bonded in a 1-coordinate geometry to five Ba2+ and one Fe3+ atom. In the tenth O2- site, O2- is bonded in a 6-coordinate geometry to two Ba2+, one Sr2+, one La3+, and two Fe3+ atoms. In the eleventh O2- site, O2- is bonded in a 6-coordinate geometry to two Ba2+, two La3+, and two Fe3+ atoms. In the twelfth O2- site, O2- is bonded in a 6-coordinate geometry to two Ba2+, one Sr2+, one La3+, and two Fe3+ atoms. In the thirteenth O2- site, O2- is bonded to three Ba2+, two equivalent La3+, and one Fe3+ atom to form distorted OBa3La2Fe octahedra that share corners with two equivalent OBa3La2Fe octahedra and faces with two OBa3SrLaFe octahedra. The corner-sharing octahedral tilt angles are 33°. In the fourteenth O2- site, O2- is bonded to three Ba2+, one Sr2+, one La3+, and one Fe3+ atom to form distorted OBa3SrLaFe octahedra that share corners with two equivalent OBa3SrLaFe octahedra and faces with two OBa3La2Fe octahedra. The corner-sharing octahedral tilt angles are 33°. In the fifteenth O2- site, O2- is bonded to three Ba2+, one Sr2+, one La3+, and one Fe3+ atom to form distorted OBa3SrLaFe octahedra that share corners with two equivalent OBa3SrLaFe octahedra and faces with two OBa3La2Fe octahedra. The corner-sharing octahedral tilt angles are 33°.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Ba5SrLa2Fe4O15 by Materials Project. https://doi.org/10.17188/1708672

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗