Materials Data on PuMnAl by Materials Project

Abstract

PuMnAl is Frank-Kasper $\mu$ Phase-derived structured and crystallizes in the orthorhombic Amm2 space group. The structure is three-dimensional. there are seven inequivalent Pu sites. In the first Pu site, Pu is bonded in a 12-coordinate geometry to four Pu, five Mn, and seven Al atoms. There are a spread of Pu–Pu bond distances ranging from 3.28–3.44 Å. There are a spread of Pu–Mn bond distances ranging from 2.99–3.23 Å. There are three shorter (3.16 Å) and four longer (3.19 Å) Pu–Al bond lengths. In the second Pu site, Pu is bonded in a 9-coordinate geometry to four Pu, seven Mn, and five Al atoms. There are one shorter (2.89 Å) and two longer (3.34 Å) Pu–Pu bond lengths. There are a spread of Pu–Mn bond distances ranging from 3.03–3.24 Å. There are one shorter (3.11 Å) and four longer (3.23 Å) Pu–Al bond lengths. In the third Pu site, Pu is bonded in a 9-coordinate geometry to four Pu, seven Mn, and five Al atoms. There are one shorter (3.28 Å) and two longer (3.34 Å) Pu–Pu bond lengths. There are a spread of Pu–Mn bond distances ranging from 3.03–3.24 Å. There are one shorter (3.11 Å) and four longer (3.23 Å) Pu–Al bond lengths. In the fourth Pu site, Pu is bonded in a 12-coordinate geometry to four Pu, five Mn, and seven Al atoms. Both Pu–Pu bond lengths are 3.34 Å. There are a spread of Pu–Mn bond distances ranging from 2.99–3.23 Å. There are three shorter (3.16 Å) and four longer (3.19 Å) Pu–Al bond lengths. In the fifth Pu site, Pu is bonded in a 12-coordinate geometry to four Pu, five Mn, and seven Al atoms. The Pu–Pu bond length is 3.44 Å. There are a spread of Pu–Mn bond distances ranging from 2.99–3.23 Å. There are three shorter (3.16 Å) and four longer (3.19 Å) Pu–Al bond lengths. In the sixth Pu site, Pu is bonded in a 9-coordinate geometry to four Pu, seven Mn, and five Al atoms. There are one shorter (2.89 Å) and one longer (3.28 Å) Pu–Pu bond lengths. There are a spread of Pu–Mn bond distances ranging from 3.03–3.24 Å. There are one shorter (3.11 Å) and four longer (3.23 Å) Pu–Al bond lengths. In the seventh Pu site, Pu is bonded in a 12-coordinate geometry to four Pu, five Mn, and seven Al atoms. There are a spread of Pu–Mn bond distances ranging from 2.99–3.23 Å. There are three shorter (3.16 Å) and four longer (3.19 Å) Pu–Al bond lengths. There are three inequivalent Mn sites. In the first Mn site, Mn is bonded to six Pu and six Al atoms to form MnPu6Al6 cuboctahedra that share corners with four equivalent AlPu6Mn4Al2 cuboctahedra, corners with fourteen MnPu6Al6 cuboctahedra, edges with six MnPu6Al6 cuboctahedra, faces with four equivalent MnPu6Mn4Al2 cuboctahedra, and faces with fourteen AlPu6Mn4Al2 cuboctahedra. There are a spread of Mn–Al bond distances ranging from 2.65–2.71 Å. In the second Mn site, Mn is bonded to six Pu, four Mn, and two equivalent Al atoms to form MnPu6Mn4Al2 cuboctahedra that share corners with eight MnPu6Al6 cuboctahedra, corners with ten AlPu6Mn4Al2 cuboctahedra, edges with two equivalent MnPu6Mn4Al2 cuboctahedra, edges with four equivalent AlPu6Mn2Al4 cuboctahedra, faces with eight AlPu6Mn4Al2 cuboctahedra, and faces with ten MnPu6Al6 cuboctahedra. There are a spread of Mn–Mn bond distances ranging from 2.67–2.77 Å. Both Mn–Al bond lengths are 2.62 Å. In the third Mn site, Mn is bonded to six Pu, four equivalent Mn, and two equivalent Al atoms to form MnPu6Mn4Al2 cuboctahedra that share corners with six MnPu6Al6 cuboctahedra, corners with twelve AlPu6Mn4Al2 cuboctahedra, edges with six MnPu6Al6 cuboctahedra, faces with eight equivalent MnPu6Mn4Al2 cuboctahedra, and faces with ten AlPu6Mn4Al2 cuboctahedra. Both Mn–Al bond lengths are 2.61 Å. There are two inequivalent Al sites. In the first Al site, Al is bonded to six Pu, four Mn, and two equivalent Al atoms to form AlPu6Mn4Al2 cuboctahedra that share corners with four equivalent AlPu6Mn2Al4 cuboctahedra, corners with eight MnPu6Al6 cuboctahedra, edges with six equivalent AlPu6Mn4Al2 cuboctahedra, faces with eight AlPu6Mn4Al2 cuboctahedra, and faces with twelve MnPu6Al6 cuboctahedra. Both Al–Al bond lengths are 2.74 Å. In the second Al site, Al is bonded to six Pu, two equivalent Mn, and four Al atoms to form AlPu6Mn2Al4 cuboctahedra that share corners with eight AlPu6Mn4Al2 cuboctahedra, corners with ten MnPu6Mn4Al2 cuboctahedra, edges with two equivalent AlPu6Mn2Al4 cuboctahedra, edges with four equivalent MnPu6Mn4Al2 cuboctahedra, faces with eight MnPu6Al6 cuboctahedra, and faces with ten AlPu6Mn4Al2 cuboctahedra. There are one shorter (2.67 Å) and one longer (2.81 Å) Al–Al bond lengths.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-06-04. Materials Data on PuMnAl by Materials Project. https://doi.org/10.17188/1717171

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗