Materials Data on Al3(SiO5)2 by Materials Project

Abstract

Al3(SiO5)2 crystallizes in the triclinic P1 space group. The structure is three-dimensional. there are six inequivalent Al sites. In the first Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five SiO4 tetrahedra and edges with three AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.88–1.96 Å. In the second Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five SiO4 tetrahedra and edges with three AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.88–1.97 Å. In the third Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with four SiO4 tetrahedra and edges with two AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.86–1.96 Å. In the fourth Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five SiO4 tetrahedra and edges with three AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.88–1.96 Å. In the fifth Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five SiO4 tetrahedra and edges with three AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.88–1.97 Å. In the sixth Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with four SiO4 tetrahedra and edges with two AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.85–1.96 Å. There are four inequivalent Si sites. In the first Si site, Si is bonded to four O atoms to form SiO4 tetrahedra that share corners with seven AlO6 octahedra. The corner-sharing octahedra tilt angles range from 44–56°. There are a spread of Si–O bond distances ranging from 1.63–1.67 Å. In the second Si site, Si is bonded to four O atoms to form SiO4 tetrahedra that share corners with seven AlO6 octahedra. The corner-sharing octahedra tilt angles range from 44–56°. There are a spread of Si–O bond distances ranging from 1.63–1.67 Å. In the third Si site, Si is bonded to four O atoms to form SiO4 tetrahedra that share corners with seven AlO6 octahedra. The corner-sharing octahedra tilt angles range from 45–56°. There are a spread of Si–O bond distances ranging from 1.63–1.67 Å. In the fourth Si site, Si is bonded to four O atoms to form SiO4 tetrahedra that share corners with seven AlO6 octahedra. The corner-sharing octahedra tilt angles range from 43–56°. There are a spread of Si–O bond distances ranging from 1.63–1.67 Å. There are twenty inequivalent O sites. In the first O site, O is bonded in a trigonal planar geometry to two Al and one Si atom. In the second O site, O is bonded in a distorted trigonal planar geometry to two Al and one Si atom. In the third O site, O is bonded in a distorted trigonal planar geometry to two Al and one Si atom. In the fourth O site, O is bonded in a bent 150 degrees geometry to one Al and one Si atom. In the fifth O site, O is bonded in a distorted trigonal planar geometry to two Al and one Si atom. In the sixth O site, O is bonded in a trigonal planar geometry to two Al and one Si atom. In the seventh O site, O is bonded in a distorted bent 150 degrees geometry to one Al and one Si atom. In the eighth O site, O is bonded in a distorted trigonal planar geometry to two Al and one Si atom. In the ninth O site, O is bonded in a water-like geometry to two Al atoms. In the tenth O site, O is bonded in a water-like geometry to two Al atoms. In the eleventh O site, O is bonded in a trigonal planar geometry to two Al and one Si atom. In the twelfth O site, O is bonded in a distorted trigonal planar geometry to two Al and one Si atom. In the thirteenth O site, O is bonded in a distorted trigonal planar geometry to two Al and one Si atom. In the fourteenth O site, O is bonded in a distorted bent 150 degrees geometry to one Al and one Si atom. In the fifteenth O site, O is bonded in a distorted trigonal planar geometry to two Al and one Si atom. In the sixteenth O site, O is bonded in a trigonal planar geometry to two Al and one Si atom. In the seventeenth O site, O is bonded in a bent 150 degrees geometry to one Al and one Si atom. In the eighteenth O site, O is bonded in a distorted trigonal planar geometry to two Al and one Si atom. In the nineteenth O site, O is bonded in a water-like geometry to two Al atoms. In the twentieth O site, O is bonded in a water-like geometry to two Al atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Al3(SiO5)2 by Materials Project. https://doi.org/10.17188/1719217

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗