Materials Data on RuRh4 by Materials Project

Abstract

RuRh4 is alpha La-derived structured and crystallizes in the trigonal R-3m space group. The structure is three-dimensional. Ru is bonded to six equivalent Ru and six equivalent Rh atoms to form RuRu6Rh6 cuboctahedra that share corners with six equivalent RuRu6Rh6 cuboctahedra, corners with six RhRh12 cuboctahedra, edges with six equivalent RuRu6Rh6 cuboctahedra, edges with eighteen RhRh12 cuboctahedra, faces with six equivalent RuRu6Rh6 cuboctahedra, and faces with twelve equivalent RhRu3Rh9 cuboctahedra. All Ru–Ru bond lengths are 2.72 Å. All Ru–Rh bond lengths are 2.68 Å. There are four inequivalent Rh sites. In the first Rh site, Rh is bonded to three equivalent Ru and nine Rh atoms to form RhRu3Rh9 cuboctahedra that share corners with twelve RhRu3Rh9 cuboctahedra, edges with six equivalent RuRu6Rh6 cuboctahedra, edges with eighteen RhRu3Rh9 cuboctahedra, faces with six equivalent RuRu6Rh6 cuboctahedra, and faces with twelve RhRu3Rh9 cuboctahedra. There are six shorter (2.72 Å) and three longer (2.75 Å) Rh–Rh bond lengths. In the second Rh site, Rh is bonded to twelve Rh atoms to form RhRh12 cuboctahedra that share corners with three equivalent RuRu6Rh6 cuboctahedra, corners with nine RhRu3Rh9 cuboctahedra, edges with three equivalent RuRu6Rh6 cuboctahedra, edges with twenty-one RhRu3Rh9 cuboctahedra, and faces with eighteen RhRu3Rh9 cuboctahedra. There are three shorter (2.70 Å) and six longer (2.72 Å) Rh–Rh bond lengths. In the third Rh site, Rh is bonded to twelve Rh atoms to form RhRh12 cuboctahedra that share corners with three equivalent RuRu6Rh6 cuboctahedra, corners with nine RhRu3Rh9 cuboctahedra, edges with three equivalent RuRu6Rh6 cuboctahedra, edges with twenty-one RhRu3Rh9 cuboctahedra, and faces with eighteen RhRu3Rh9 cuboctahedra. There are six shorter (2.72 Å) and three longer (2.75 Å) Rh–Rh bond lengths. In the fourth Rh site, Rh is bonded to twelve Rh atoms to form RhRh12 cuboctahedra that share corners with three equivalent RuRu6Rh6 cuboctahedra, corners with nine RhRh12 cuboctahedra, edges with three equivalent RuRu6Rh6 cuboctahedra, edges with twenty-one RhRh12 cuboctahedra, and faces with eighteen RhRh12 cuboctahedra. There are a spread of Rh–Rh bond distances ranging from 2.70–2.75 Å.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-03. Materials Data on RuRh4 by Materials Project. https://doi.org/10.17188/1719846

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗