Materials Data on Ce4Ni4Bi3Sb5 by Materials Project

Abstract

Ce4Ni4Bi3Sb5 is Parent of FeAs superconductors-like structured and crystallizes in the orthorhombic Pmm2 space group. The structure is three-dimensional. there are four inequivalent Ce sites. In the first Ce site, Ce is bonded in a 12-coordinate geometry to four Ni, four Bi, and four equivalent Sb atoms. All Ce–Ni bond lengths are 3.11 Å. All Ce–Bi bond lengths are 3.48 Å. All Ce–Sb bond lengths are 3.28 Å. In the second Ce site, Ce is bonded to four Ni, two equivalent Bi, and six Sb atoms to form distorted CeNi4Bi2Sb6 cuboctahedra that share corners with four equivalent CeNi4Bi2Sb6 cuboctahedra, corners with four equivalent BiCe4Sb4 hexagonal bipyramids, corners with four equivalent SbCe4Bi4 hexagonal bipyramids, edges with four equivalent CeNi4Bi2Sb6 cuboctahedra, edges with two equivalent BiCe4Sb4 hexagonal bipyramids, edges with two equivalent SbCe4Bi4 hexagonal bipyramids, and faces with four equivalent CeNi4Bi2Sb6 cuboctahedra. All Ce–Ni bond lengths are 3.15 Å. Both Ce–Bi bond lengths are 3.44 Å. There are four shorter (3.29 Å) and two longer (3.44 Å) Ce–Sb bond lengths. In the third Ce site, Ce is bonded to four Ni, two equivalent Bi, and six Sb atoms to form distorted CeNi4Bi2Sb6 cuboctahedra that share corners with four equivalent CeNi4Bi2Sb6 cuboctahedra, corners with four equivalent BiCe4Sb4 hexagonal bipyramids, corners with four equivalent SbCe4Bi4 hexagonal bipyramids, edges with four equivalent CeNi4Bi2Sb6 cuboctahedra, edges with two equivalent BiCe4Sb4 hexagonal bipyramids, edges with two equivalent SbCe4Bi4 hexagonal bipyramids, and faces with four equivalent CeNi4Bi2Sb6 cuboctahedra. There are two shorter (3.15 Å) and two longer (3.16 Å) Ce–Ni bond lengths. Both Ce–Bi bond lengths are 3.42 Å. There are four shorter (3.29 Å) and two longer (3.43 Å) Ce–Sb bond lengths. In the fourth Ce site, Ce is bonded in a 12-coordinate geometry to four Ni, four Bi, and four equivalent Sb atoms. All Ce–Ni bond lengths are 3.10 Å. All Ce–Bi bond lengths are 3.48 Å. All Ce–Sb bond lengths are 3.28 Å. There are four inequivalent Ni sites. In the first Ni site, Ni is bonded in a distorted body-centered cubic geometry to four Ce and four Sb atoms. There are two shorter (2.61 Å) and two longer (2.62 Å) Ni–Sb bond lengths. In the second Ni site, Ni is bonded in a distorted body-centered cubic geometry to four Ce and four Sb atoms. There are two shorter (2.61 Å) and two longer (2.62 Å) Ni–Sb bond lengths. In the third Ni site, Ni is bonded in a distorted body-centered cubic geometry to four Ce and four Sb atoms. There are two shorter (2.61 Å) and two longer (2.62 Å) Ni–Sb bond lengths. In the fourth Ni site, Ni is bonded in a distorted body-centered cubic geometry to four Ce and four Sb atoms. All Ni–Sb bond lengths are 2.61 Å. There are three inequivalent Bi sites. In the first Bi site, Bi is bonded in a 8-coordinate geometry to four Ce and four equivalent Bi atoms. All Bi–Bi bond lengths are 3.18 Å. In the second Bi site, Bi is bonded to four Ce and four equivalent Sb atoms to form distorted BiCe4Sb4 hexagonal bipyramids that share corners with eight CeNi4Bi2Sb6 cuboctahedra, corners with four equivalent BiCe4Sb4 hexagonal bipyramids, edges with four CeNi4Bi2Sb6 cuboctahedra, edges with four equivalent SbCe4Bi4 hexagonal bipyramids, and faces with four equivalent BiCe4Sb4 hexagonal bipyramids. All Bi–Sb bond lengths are 3.18 Å. In the third Bi site, Bi is bonded in a 8-coordinate geometry to four Ce and four equivalent Bi atoms. There are five inequivalent Sb sites. In the first Sb site, Sb is bonded in a 9-coordinate geometry to four equivalent Ce and four Ni atoms. In the second Sb site, Sb is bonded in a 9-coordinate geometry to four equivalent Ce and four Ni atoms. In the third Sb site, Sb is bonded in a 9-coordinate geometry to four equivalent Ce and four Ni atoms. In the fourth Sb site, Sb is bonded in a 9-coordinate geometry to four equivalent Ce and four Ni atoms. In the fifth Sb site, Sb is bonded to four Ce and four equivalent Bi atoms to form distorted SbCe4Bi4 hexagonal bipyramids that share corners with eight CeNi4Bi2Sb6 cuboctahedra, corners with four equivalent SbCe4Bi4 hexagonal bipyramids, edges with four CeNi4Bi2Sb6 cuboctahedra, edges with four equivalent BiCe4Sb4 hexagonal bipyramids, and faces with four equivalent SbCe4Bi4 hexagonal bipyramids.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Ce4Ni4Bi3Sb5 by Materials Project. https://doi.org/10.17188/1720810

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗