Materials Data on Ba6Ca12Cu15Hg3O37 by Materials Project

Abstract

Ba6Ca12Cu15Hg3O37 crystallizes in the monoclinic C2/m space group. The structure is three-dimensional. there are three inequivalent Ba2+ sites. In the first Ba2+ site, Ba2+ is bonded in a 9-coordinate geometry to nine O2- atoms. There are a spread of Ba–O bond distances ranging from 2.65–2.95 Å. In the second Ba2+ site, Ba2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Ba–O bond distances ranging from 2.78–2.83 Å. In the third Ba2+ site, Ba2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Ba–O bond distances ranging from 2.77–2.83 Å. There are six inequivalent Ca2+ sites. In the first Ca2+ site, Ca2+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.42–2.57 Å. In the second Ca2+ site, Ca2+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.42–2.55 Å. In the third Ca2+ site, Ca2+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.42–2.55 Å. In the fourth Ca2+ site, Ca2+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.49–2.53 Å. In the fifth Ca2+ site, Ca2+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are four shorter (2.49 Å) and four longer (2.52 Å) Ca–O bond lengths. In the sixth Ca2+ site, Ca2+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are four shorter (2.49 Å) and four longer (2.52 Å) Ca–O bond lengths. There are eight inequivalent Cu+2.13+ sites. In the first Cu+2.13+ site, Cu+2.13+ is bonded in a rectangular see-saw-like geometry to four O2- atoms. All Cu–O bond lengths are 1.93 Å. In the second Cu+2.13+ site, Cu+2.13+ is bonded in a rectangular see-saw-like geometry to four O2- atoms. There is two shorter (1.92 Å) and two longer (1.93 Å) Cu–O bond length. In the third Cu+2.13+ site, Cu+2.13+ is bonded in a rectangular see-saw-like geometry to four O2- atoms. All Cu–O bond lengths are 1.93 Å. In the fourth Cu+2.13+ site, Cu+2.13+ is bonded in a rectangular see-saw-like geometry to five O2- atoms. There are a spread of Cu–O bond distances ranging from 1.92–2.79 Å. In the fifth Cu+2.13+ site, Cu+2.13+ is bonded in a distorted square co-planar geometry to five O2- atoms. There are four shorter (1.93 Å) and one longer (2.76 Å) Cu–O bond lengths. In the sixth Cu+2.13+ site, Cu+2.13+ is bonded in a rectangular see-saw-like geometry to five O2- atoms. There are a spread of Cu–O bond distances ranging from 1.92–2.79 Å. In the seventh Cu+2.13+ site, Cu+2.13+ is bonded in a square co-planar geometry to four O2- atoms. All Cu–O bond lengths are 1.93 Å. In the eighth Cu+2.13+ site, Cu+2.13+ is bonded in a square co-planar geometry to four equivalent O2- atoms. All Cu–O bond lengths are 1.93 Å. There are two inequivalent Hg2+ sites. In the first Hg2+ site, Hg2+ is bonded in a square co-planar geometry to four O2- atoms. There are two shorter (2.06 Å) and two longer (2.73 Å) Hg–O bond lengths. In the second Hg2+ site, Hg2+ is bonded in a T-shaped geometry to three O2- atoms. There are a spread of Hg–O bond distances ranging from 2.04–2.64 Å. There are eleven inequivalent O2- sites. In the first O2- site, O2- is bonded in a 1-coordinate geometry to four Ba2+, one Cu+2.13+, and one Hg2+ atom. In the second O2- site, O2- is bonded in a 6-coordinate geometry to four Ba2+, one Cu+2.13+, and one Hg2+ atom. In the third O2- site, O2- is bonded to four Ca2+ and two Cu+2.13+ atoms to form distorted OCa4Cu2 octahedra that share corners with ten OBa2Ca2Cu2 octahedra, edges with three OCa4Cu2 octahedra, and faces with four OCa4Cu2 octahedra. The corner-sharing octahedra tilt angles range from 1–66°. In the fourth O2- site, O2- is bonded to four Ca2+ and two Cu+2.13+ atoms to form distorted OCa4Cu2 octahedra that share corners with ten OBa2Ca2Cu2 octahedra, edges with three OCa4Cu2 octahedra, and faces with four OCa4Cu2 octahedra. The corner-sharing octahedra tilt angles range from 1–66°. In the fifth O2- site, O2- is bonded to four Ca2+ and two Cu+2.13+ atoms to form distorted OCa4Cu2 octahedra that share corners with ten OBa2Ca2Cu2 octahedra, edges with four OBa2Ca2Cu2 octahedra, and faces with four OCa4Cu2 octahedra. The corner-sharing octahedra tilt angles range from 1–66°. In the sixth O2- site, O2- is bonded to four Ca2+ and two equivalent Cu+2.13+ atoms to form a mixture of corner, edge, and face-sharing OCa4Cu2 octahedra. The corner-sharing octahedra tilt angles range from 0–66°. In the seventh O2- site, O2- is bonded to four Ca2+ and two Cu+2.13+ atoms to form a mixture of corner, edge, and face-sharing OCa4Cu2 octahedra. The corner-sharing octahedra tilt angles range from 0–66°. In the eighth O2- site, O2- is bonded in a 6-coordinate geometry to two Ba2+, two Ca2+, and two Cu+2.13+ atoms. In the ninth O2- site, O2- is bonded in a 6-coordinate geometry to two Ba2+, two Ca2+, and two Cu+2.13+ atoms. In the tenth O2- site, O2- is bonded to two Ba2+, two Ca2+, and two Cu+2.13+ atoms to form distorted OBa2Ca2Cu2 octahedra that share corners with six OCa4Cu2 octahedra, an edgeedge with one OCa4Cu2 octahedra, and faces with two equivalent OBa2Ca2Cu2 octahedra. The corner-sharing octahedra tilt angles range from 3–66°. In the eleventh O2- site, O2- is bonded to two equivalent Ba2+ and four Hg2+ atoms to form corner-sharing OBa2Hg4 octahedra. The corner-sharing octahedral tilt angles are 0°.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Ba6Ca12Cu15Hg3O37 by Materials Project. https://doi.org/10.17188/1723185

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗