Materials Data on GdTm(FeNi4)2 by Materials Project

Abstract

TmGd(FeNi4)2 crystallizes in the orthorhombic Pmm2 space group. The structure is three-dimensional. Tm is bonded in a 6-coordinate geometry to three Fe and fifteen Ni atoms. There are one shorter (2.82 Å) and two longer (2.83 Å) Tm–Fe bond lengths. There are a spread of Tm–Ni bond distances ranging from 2.83–3.15 Å. Gd is bonded in a 6-coordinate geometry to three Fe and fifteen Ni atoms. There are two shorter (2.85 Å) and one longer (2.86 Å) Gd–Fe bond lengths. There are a spread of Gd–Ni bond distances ranging from 2.85–3.17 Å. There are two inequivalent Fe sites. In the first Fe site, Fe is bonded to two equivalent Tm, one Gd, and nine Ni atoms to form distorted FeGdTm2Ni9 cuboctahedra that share corners with twenty-one NiGd2TmFe3Ni6 cuboctahedra, edges with six FeGdTm2Ni9 cuboctahedra, faces with two equivalent FeGdTm2Ni9 cuboctahedra, and faces with twenty-one NiGd2TmFe3Ni6 cuboctahedra. There are a spread of Fe–Ni bond distances ranging from 2.42–2.84 Å. In the second Fe site, Fe is bonded to one Tm, two equivalent Gd, and nine Ni atoms to form distorted FeGd2TmNi9 cuboctahedra that share corners with twenty-one NiGd2TmFe3Ni6 cuboctahedra, edges with six FeGdTm2Ni9 cuboctahedra, faces with two equivalent FeGd2TmNi9 cuboctahedra, and faces with twenty-one NiGd2TmFe3Ni6 cuboctahedra. There are a spread of Fe–Ni bond distances ranging from 2.42–2.87 Å. There are six inequivalent Ni sites. In the first Ni site, Ni is bonded to one Tm, two equivalent Gd, three Fe, and six Ni atoms to form distorted NiGd2TmFe3Ni6 cuboctahedra that share corners with nine FeGdTm2Ni9 cuboctahedra, corners with twelve NiGd4Fe2Ni6 cuboctahedra, edges with six NiGd2TmFe3Ni6 cuboctahedra, faces with three FeGdTm2Ni9 cuboctahedra, and faces with twenty NiGd2TmFe3Ni6 cuboctahedra. There are four shorter (2.42 Å) and two longer (2.43 Å) Ni–Ni bond lengths. In the second Ni site, Ni is bonded to two equivalent Tm, one Gd, three Fe, and six Ni atoms to form distorted NiGdTm2Fe3Ni6 cuboctahedra that share corners with nine FeGdTm2Ni9 cuboctahedra, corners with twelve NiTm4Fe2Ni6 cuboctahedra, edges with six NiGd2TmFe3Ni6 cuboctahedra, faces with three FeGdTm2Ni9 cuboctahedra, and faces with twenty NiGdTm2Fe3Ni6 cuboctahedra. There are two shorter (2.41 Å) and four longer (2.43 Å) Ni–Ni bond lengths. In the third Ni site, Ni is bonded to four equivalent Tm, two equivalent Fe, and six Ni atoms to form distorted NiTm4Fe2Ni6 cuboctahedra that share corners with four equivalent FeGdTm2Ni9 cuboctahedra, corners with twenty NiGdTm2Fe3Ni6 cuboctahedra, edges with ten NiGd2Tm2Fe2Ni6 cuboctahedra, faces with six FeGdTm2Ni9 cuboctahedra, and faces with sixteen NiGd2TmFe3Ni6 cuboctahedra. There are two shorter (2.44 Å) and two longer (2.45 Å) Ni–Ni bond lengths. In the fourth Ni site, Ni is bonded to four equivalent Gd, two equivalent Fe, and six Ni atoms to form NiGd4Fe2Ni6 cuboctahedra that share corners with four equivalent FeGd2TmNi9 cuboctahedra, corners with twenty NiGd2TmFe3Ni6 cuboctahedra, edges with ten NiGd2Tm2Fe2Ni6 cuboctahedra, faces with six FeGdTm2Ni9 cuboctahedra, and faces with sixteen NiGd2TmFe3Ni6 cuboctahedra. There are two shorter (2.47 Å) and two longer (2.48 Å) Ni–Ni bond lengths. In the fifth Ni site, Ni is bonded to two equivalent Tm, two equivalent Gd, two equivalent Fe, and six Ni atoms to form distorted NiGd2Tm2Fe2Ni6 cuboctahedra that share corners with four equivalent FeGd2TmNi9 cuboctahedra, corners with twenty NiGdTm2Fe3Ni6 cuboctahedra, edges with ten NiGd2Tm2Fe2Ni6 cuboctahedra, faces with six FeGdTm2Ni9 cuboctahedra, and faces with sixteen NiGd2TmFe3Ni6 cuboctahedra. There are one shorter (2.43 Å) and one longer (2.49 Å) Ni–Ni bond lengths. In the sixth Ni site, Ni is bonded to two equivalent Tm, two equivalent Gd, two equivalent Fe, and six Ni atoms to form distorted NiGd2Tm2Fe2Ni6 cuboctahedra that share corners with four equivalent FeGdTm2Ni9 cuboctahedra, corners with twenty NiGd2TmFe3Ni6 cuboctahedra, edges with ten NiGd2Tm2Fe2Ni6 cuboctahedra, faces with six FeGdTm2Ni9 cuboctahedra, and faces with sixteen NiGd2TmFe3Ni6 cuboctahedra. There are one shorter (2.45 Å) and one longer (2.47 Å) Ni–Ni bond lengths.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-03. Materials Data on GdTm(FeNi4)2 by Materials Project. https://doi.org/10.17188/1723433

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗