Materials Data on Na3CaFe4(SiO3)8 by Materials Project

Abstract

Na3CaFe4(SiO3)8 is Esseneite-derived structured and crystallizes in the triclinic P1 space group. The structure is three-dimensional. there are nine inequivalent Na1+ sites. In the first Na1+ site, Na1+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.41–2.86 Å. In the second Na1+ site, Na1+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.41–2.86 Å. In the third Na1+ site, Na1+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.41–2.90 Å. In the fourth Na1+ site, Na1+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.38–2.90 Å. In the fifth Na1+ site, Na1+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.40–2.86 Å. In the sixth Na1+ site, Na1+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.40–2.87 Å. In the seventh Na1+ site, Na1+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.39–2.87 Å. In the eighth Na1+ site, Na1+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.41–2.87 Å. In the ninth Na1+ site, Na1+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.41–2.92 Å. There are three inequivalent Ca2+ sites. In the first Ca2+ site, Ca2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.32–2.84 Å. In the second Ca2+ site, Ca2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.31–2.81 Å. In the third Ca2+ site, Ca2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.32–2.83 Å. There are twelve inequivalent Fe+2.75+ sites. In the first Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 2.02–2.19 Å. In the second Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 2.02–2.21 Å. In the third Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 1.95–2.13 Å. In the fourth Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 1.95–2.13 Å. In the fifth Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 1.97–2.12 Å. In the sixth Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 2.03–2.23 Å. In the seventh Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 1.97–2.17 Å. In the eighth Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 1.96–2.21 Å. In the ninth Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 1.98–2.17 Å. In the tenth Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 1.96–2.20 Å. In the eleventh Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 1.97–2.17 Å. In the twelfth Fe+2.75+ site, Fe+2.75+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with six SiO4 tetrahedra and edges with two FeO6 octahedra. There are a spread of Fe–O bond distances ranging from 1.96–2.20 Å. There are twenty-four inequivalent Si4+ sites. In the first Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 34–59°. There are a spread of Si–O bond distances ranging from 1.59–1.68 Å. In the second Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 37–59°. There are a spread of Si–O bond distances ranging from 1.61–1.69 Å. In the third Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 34–61°. There are a spread of Si–O bond distances ranging from 1.63–1.69 Å. In the fourth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 32–60°. There is two shorter (1.62 Å) and two longer (1.68 Å) Si–O bond length. In the fifth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 34–59°. There is one shorter (1.61 Å) and three longer (1.66 Å) Si–O bond length. In the sixth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 34–57°. There are a spread of Si–O bond distances ranging from 1.62–1.67 Å. In the seventh Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 34–59°. There are a spread of Si–O bond distances ranging from 1.63–1.68 Å. In the eighth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 32–60°. There are a spread of Si–O bond distances ranging from 1.62–1.68 Å. In the ninth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 32–59°. There are a spread of Si–O bond distances ranging from 1.62–1.67 Å. In the tenth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 34–59°. There are a spread of Si–O bond distances ranging from 1.63–1.68 Å. In the eleventh Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 35–59°. There are a spread of Si–O bond distances ranging from 1.59–1.68 Å. In the twelfth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 35–60°. There are a spread of Si–O bond distances ranging from 1.61–1.67 Å. In the thirteenth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 38–60°. There are a spread of Si–O bond distances ranging from 1.60–1.69 Å. In the fourteenth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 32–64°. There are a spread of Si–O bond distances ranging from 1.62–1.67 Å. In the fifteenth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 33–61°. There are a spread of Si–O bond distances ranging from 1.62–1.69 Å. In the sixteenth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 34–61°. There is two shorter (1.62 Å) and two longer (1.68 Å) Si–O bond length. In the seventeenth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 33–64°. There are a spread of Si–O bond distances ranging from 1.62–1.68 Å. In the eighteenth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 35–57°. There are a spread of Si–O bond distances ranging from 1.61–1.68 Å. In the nineteenth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 38–60°. There are a spread of Si–O bond distances ranging from 1.60–1.69 Å. In the twentieth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 34–59°. There are a spread of Si–O bond distances ranging from 1.60–1.68 Å. In the twenty-first Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 32–61°. There are a spread of Si–O bond distances ranging from 1.62–1.68 Å. In the twenty-second Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 35–58°. There are a spread of Si–O bond distances ranging from 1.61–1.68 Å. In the twenty-third Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 33–59°. There are a spread of Si–O bond distances ranging from 1.61–1.67 Å. In the twenty-fourth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three FeO6 octahedra and corners with two SiO4 tetrahedra. The corner-sharing octahedra tilt angles range f