Materials Data on W by Materials Project

Abstract

W crystallizes in the monoclinic P2/m space group. The structure is three-dimensional. there are ten inequivalent W sites. In the first W site, W is bonded to eight W atoms to form distorted WW8 hexagonal bipyramids that share corners with six WW8 hexagonal bipyramids, corners with two WW7 hexagonal pyramids, edges with twenty-two WW8 hexagonal bipyramids, and edges with two WW7 hexagonal pyramids. There are a spread of W–W bond distances ranging from 2.63–3.04 Å. In the second W site, W is bonded to eight W atoms to form distorted WW8 hexagonal bipyramids that share corners with five WW8 hexagonal bipyramids, corners with three WW7 hexagonal pyramids, edges with twenty-three WW8 hexagonal bipyramids, and an edgeedge with one WW7 hexagonal pyramid. There are a spread of W–W bond distances ranging from 2.63–3.06 Å. In the third W site, W is bonded to eight W atoms to form distorted WW8 hexagonal bipyramids that share corners with seven WW8 hexagonal bipyramids, edges with nineteen WW8 hexagonal bipyramids, and edges with five WW7 hexagonal pyramids. There are a spread of W–W bond distances ranging from 2.63–3.04 Å. In the fourth W site, W is bonded to eight W atoms to form distorted WW8 hexagonal bipyramids that share corners with six WW8 hexagonal bipyramids, corners with two equivalent WW7 hexagonal pyramids, edges with seventeen WW8 hexagonal bipyramids, and edges with six WW7 hexagonal pyramids. There are a spread of W–W bond distances ranging from 2.63–3.01 Å. In the fifth W site, W is bonded to eight W atoms to form distorted WW8 hexagonal bipyramids that share corners with six WW8 hexagonal bipyramids, a cornercorner with one WW7 hexagonal pyramid, edges with eighteen WW8 hexagonal bipyramids, and edges with six WW7 hexagonal pyramids. There are a spread of W–W bond distances ranging from 2.63–3.00 Å. In the sixth W site, W is bonded to eight W atoms to form distorted WW8 hexagonal bipyramids that share corners with five WW8 hexagonal bipyramids, corners with three WW7 hexagonal pyramids, edges with sixteen WW8 hexagonal bipyramids, and edges with seven WW7 hexagonal pyramids. There are a spread of W–W bond distances ranging from 2.63–2.97 Å. In the seventh W site, W is bonded to seven W atoms to form distorted WW7 hexagonal pyramids that share corners with five WW8 hexagonal bipyramids, corners with six WW7 hexagonal pyramids, edges with thirteen WW8 hexagonal bipyramids, and edges with four WW7 hexagonal pyramids. There are a spread of W–W bond distances ranging from 2.63–2.67 Å. In the eighth W site, W is bonded to seven W atoms to form distorted WW7 hexagonal pyramids that share corners with four WW8 hexagonal bipyramids, corners with seven WW7 hexagonal pyramids, edges with thirteen WW8 hexagonal bipyramids, and edges with four WW7 hexagonal pyramids. There are a spread of W–W bond distances ranging from 2.63–2.67 Å. In the ninth W site, W is bonded to eight W atoms to form distorted WW8 hexagonal bipyramids that share corners with five WW8 hexagonal bipyramids, corners with two equivalent WW7 hexagonal pyramids, edges with twelve WW8 hexagonal bipyramids, and edges with eleven WW7 hexagonal pyramids. There are a spread of W–W bond distances ranging from 2.63–3.05 Å. In the tenth W site, W is bonded to seven W atoms to form distorted WW7 hexagonal pyramids that share corners with four WW8 hexagonal bipyramids, corners with seven WW7 hexagonal pyramids, edges with twelve WW8 hexagonal bipyramids, and edges with five WW7 hexagonal pyramids. Both W–W bond lengths are 2.63 Å.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-03. Materials Data on W by Materials Project. https://doi.org/10.17188/1731927

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗