Materials Data on Hf4ZnGa11 by Materials Project

Abstract

Hf4ZnGa11 is Uranium Silicide-derived structured and crystallizes in the tetragonal P4mm space group. The structure is three-dimensional. there are four inequivalent Hf sites. In the first Hf site, Hf is bonded to twelve Ga atoms to form HfGa12 cuboctahedra that share corners with four equivalent ZnHf4Ga8 cuboctahedra, corners with eight HfGa12 cuboctahedra, edges with four equivalent HfZn4Ga8 cuboctahedra, edges with sixteen GaHf4Zn2Ga6 cuboctahedra, a faceface with one ZnHf4Ga8 cuboctahedra, faces with five HfGa12 cuboctahedra, and faces with eight GaHf4Ga8 cuboctahedra. There are a spread of Hf–Ga bond distances ranging from 2.81–3.08 Å. In the second Hf site, Hf is bonded to twelve Ga atoms to form HfGa12 cuboctahedra that share corners with eight HfGa12 cuboctahedra, edges with four equivalent HfGa12 cuboctahedra, edges with four equivalent ZnHf4Ga8 cuboctahedra, edges with sixteen GaHf4Ga8 cuboctahedra, faces with five HfGa12 cuboctahedra, and faces with eight GaHf4Zn2Ga6 cuboctahedra. There are a spread of Hf–Ga bond distances ranging from 2.81–3.04 Å. In the third Hf site, Hf is bonded to four equivalent Zn and eight Ga atoms to form HfZn4Ga8 cuboctahedra that share corners with eight HfGa12 cuboctahedra, edges with four equivalent HfGa12 cuboctahedra, edges with sixteen GaHf4Zn2Ga6 cuboctahedra, faces with four equivalent ZnHf4Ga8 cuboctahedra, faces with five HfGa12 cuboctahedra, and faces with eight GaHf4Zn2Ga6 cuboctahedra. All Hf–Zn bond lengths are 2.81 Å. There are four shorter (2.83 Å) and four longer (2.99 Å) Hf–Ga bond lengths. In the fourth Hf site, Hf is bonded to twelve Ga atoms to form HfGa12 cuboctahedra that share corners with eight HfGa12 cuboctahedra, edges with four equivalent HfGa12 cuboctahedra, edges with sixteen GaHf4Ga8 cuboctahedra, faces with five HfGa12 cuboctahedra, and faces with eight GaHf4Ga8 cuboctahedra. There are a spread of Hf–Ga bond distances ranging from 2.81–3.02 Å. Zn is bonded to four equivalent Hf and eight Ga atoms to form ZnHf4Ga8 cuboctahedra that share corners with four equivalent HfGa12 cuboctahedra, corners with four equivalent ZnHf4Ga8 cuboctahedra, edges with four equivalent HfGa12 cuboctahedra, edges with sixteen GaHf4Zn2Ga6 cuboctahedra, faces with four equivalent ZnHf4Ga8 cuboctahedra, faces with five HfGa12 cuboctahedra, and faces with eight GaHf4Zn2Ga6 cuboctahedra. There are four shorter (2.87 Å) and four longer (2.95 Å) Zn–Ga bond lengths. There are seven inequivalent Ga sites. In the first Ga site, Ga is bonded to four Hf, two equivalent Zn, and six Ga atoms to form distorted GaHf4Zn2Ga6 cuboctahedra that share corners with twelve GaHf4Zn2Ga6 cuboctahedra, edges with four equivalent ZnHf4Ga8 cuboctahedra, edges with eight HfGa12 cuboctahedra, edges with eight GaHf4Zn2Ga6 cuboctahedra, faces with two equivalent ZnHf4Ga8 cuboctahedra, faces with four HfGa12 cuboctahedra, and faces with ten GaHf4Zn2Ga6 cuboctahedra. There are four shorter (2.80 Å) and two longer (2.96 Å) Ga–Ga bond lengths. In the second Ga site, Ga is bonded to four Hf and eight Ga atoms to form distorted GaHf4Ga8 cuboctahedra that share corners with twelve GaHf4Zn2Ga6 cuboctahedra, edges with eight HfGa12 cuboctahedra, edges with eight GaHf4Zn2Ga6 cuboctahedra, faces with four HfGa12 cuboctahedra, and faces with ten GaHf4Ga8 cuboctahedra. There are a spread of Ga–Ga bond distances ranging from 2.80–3.00 Å. In the third Ga site, Ga is bonded to four Hf, two equivalent Zn, and six Ga atoms to form GaHf4Zn2Ga6 cuboctahedra that share corners with twelve GaHf4Zn2Ga6 cuboctahedra, edges with four equivalent ZnHf4Ga8 cuboctahedra, edges with eight HfGa12 cuboctahedra, edges with eight GaHf4Zn2Ga6 cuboctahedra, faces with two equivalent ZnHf4Ga8 cuboctahedra, faces with four HfGa12 cuboctahedra, and faces with ten GaHf4Zn2Ga6 cuboctahedra. There are four shorter (2.80 Å) and two longer (2.94 Å) Ga–Ga bond lengths. In the fourth Ga site, Ga is bonded to four Hf and eight Ga atoms to form GaHf4Ga8 cuboctahedra that share corners with twelve GaHf4Ga8 cuboctahedra, edges with eight HfGa12 cuboctahedra, edges with eight GaHf4Zn2Ga6 cuboctahedra, faces with four HfGa12 cuboctahedra, and faces with ten GaHf4Zn2Ga6 cuboctahedra. There are a spread of Ga–Ga bond distances ranging from 2.80–2.96 Å. In the fifth Ga site, Ga is bonded in a distorted rectangular see-saw-like geometry to four equivalent Hf and eight Ga atoms. In the sixth Ga site, Ga is bonded in a distorted rectangular see-saw-like geometry to four equivalent Hf and eight Ga atoms. In the seventh Ga site, Ga is bonded in a distorted rectangular see-saw-like geometry to four equivalent Hf and eight Ga atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Hf4ZnGa11 by Materials Project. https://doi.org/10.17188/1732276

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗