Materials Data on MgSn2 by Materials Project

Abstract

MgSn2 crystallizes in the orthorhombic Amm2 space group. The structure is three-dimensional. there are two inequivalent Mg sites. In the first Mg site, Mg is bonded to four Mg and eight Sn atoms to form distorted MgMg4Sn8 cuboctahedra that share corners with ten SnMg6 cuboctahedra, corners with twelve MgMg4Sn8 cuboctahedra, edges with three equivalent MgMg4Sn8 cuboctahedra, edges with seven SnMg6 cuboctahedra, faces with two equivalent SnMg4Sn8 cuboctahedra, and faces with six MgMg4Sn8 cuboctahedra. There are two shorter (3.34 Å) and two longer (3.39 Å) Mg–Mg bond lengths. There are six shorter (3.25 Å) and two longer (3.40 Å) Mg–Sn bond lengths. In the second Mg site, Mg is bonded to four Mg and eight Sn atoms to form distorted MgMg4Sn8 cuboctahedra that share corners with six equivalent SnMg4Sn8 cuboctahedra, corners with twelve MgMg4Sn8 cuboctahedra, edges with three equivalent MgMg4Sn8 cuboctahedra, edges with nine SnMg6 cuboctahedra, faces with two equivalent SnMg4Sn8 cuboctahedra, and faces with six MgMg4Sn8 cuboctahedra. Both Mg–Mg bond lengths are 3.34 Å. There are a spread of Mg–Sn bond distances ranging from 3.23–3.41 Å. There are four inequivalent Sn sites. In the first Sn site, Sn is bonded in a distorted water-like geometry to two equivalent Mg and four equivalent Sn atoms. All Sn–Sn bond lengths are 3.26 Å. In the second Sn site, Sn is bonded in a 12-coordinate geometry to four equivalent Mg and two equivalent Sn atoms. Both Sn–Sn bond lengths are 3.31 Å. In the third Sn site, Sn is bonded to six Mg atoms to form distorted SnMg6 cuboctahedra that share corners with four equivalent MgMg4Sn8 cuboctahedra, corners with twelve SnMg6 cuboctahedra, edges with four SnMg6 cuboctahedra, edges with ten MgMg4Sn8 cuboctahedra, and faces with two equivalent SnMg6 cuboctahedra. In the fourth Sn site, Sn is bonded to four Mg and eight Sn atoms to form distorted SnMg4Sn8 cuboctahedra that share corners with twelve MgMg4Sn8 cuboctahedra, corners with fourteen SnMg6 cuboctahedra, edges with two equivalent SnMg6 cuboctahedra, edges with six MgMg4Sn8 cuboctahedra, faces with four MgMg4Sn8 cuboctahedra, and faces with four equivalent SnMg4Sn8 cuboctahedra. Both Sn–Sn bond lengths are 3.34 Å.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-03. Materials Data on MgSn2 by Materials Project. https://doi.org/10.17188/1733225

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗