Materials Data on ZrTi(CrFe)2 by Materials Project

Abstract

ZrTi(CrFe)2 crystallizes in the monoclinic Cm space group. The structure is three-dimensional. there are two inequivalent Zr sites. In the first Zr site, Zr is bonded in a 6-coordinate geometry to three equivalent Zr, one Ti, five Cr, and seven Fe atoms. There are two shorter (3.04 Å) and one longer (3.06 Å) Zr–Zr bond lengths. The Zr–Ti bond length is 2.94 Å. There are a spread of Zr–Cr bond distances ranging from 2.90–2.97 Å. There are a spread of Zr–Fe bond distances ranging from 2.86–2.96 Å. In the second Zr site, Zr is bonded in a 12-coordinate geometry to three equivalent Zr, one Ti, seven Cr, and five Fe atoms. The Zr–Ti bond length is 2.99 Å. There are a spread of Zr–Cr bond distances ranging from 2.88–2.92 Å. There are a spread of Zr–Fe bond distances ranging from 2.89–2.93 Å. There are two inequivalent Ti sites. In the first Ti site, Ti is bonded in a 12-coordinate geometry to one Zr, three equivalent Ti, seven Cr, and five Fe atoms. There are two shorter (2.99 Å) and one longer (3.00 Å) Ti–Ti bond lengths. There are a spread of Ti–Cr bond distances ranging from 2.86–2.91 Å. There are a spread of Ti–Fe bond distances ranging from 2.75–2.86 Å. In the second Ti site, Ti is bonded in a 1-coordinate geometry to one Zr, three equivalent Ti, five Cr, and seven Fe atoms. There are a spread of Ti–Cr bond distances ranging from 2.73–2.90 Å. There are a spread of Ti–Fe bond distances ranging from 2.76–2.88 Å. There are three inequivalent Cr sites. In the first Cr site, Cr is bonded to six Ti, two equivalent Cr, and four Fe atoms to form distorted CrTi6Cr2Fe4 cuboctahedra that share corners with four equivalent CrZr3Ti3Cr4Fe2 cuboctahedra, corners with eight FeZr3Ti3Cr6 cuboctahedra, edges with six equivalent CrTi6Cr2Fe4 cuboctahedra, faces with eight CrZr6Cr2Fe4 cuboctahedra, and faces with twelve FeZr3Ti3Cr6 cuboctahedra. Both Cr–Cr bond lengths are 2.40 Å. There are a spread of Cr–Fe bond distances ranging from 2.40–2.42 Å. In the second Cr site, Cr is bonded to six Zr, two equivalent Cr, and four Fe atoms to form CrZr6Cr2Fe4 cuboctahedra that share corners with four equivalent CrZr3Ti3Cr4Fe2 cuboctahedra, corners with eight FeZr3Ti3Cr6 cuboctahedra, edges with six equivalent CrZr6Cr2Fe4 cuboctahedra, faces with eight CrTi6Cr2Fe4 cuboctahedra, and faces with twelve FeZr3Ti3Cr6 cuboctahedra. Both Cr–Cr bond lengths are 2.51 Å. There are three shorter (2.51 Å) and one longer (2.53 Å) Cr–Fe bond lengths. In the third Cr site, Cr is bonded to three Zr, three Ti, four Cr, and two equivalent Fe atoms to form distorted CrZr3Ti3Cr4Fe2 cuboctahedra that share corners with eight CrTi6Cr2Fe4 cuboctahedra, corners with ten FeZr3Ti3Cr2Fe4 cuboctahedra, edges with two equivalent CrZr3Ti3Cr4Fe2 cuboctahedra, edges with four equivalent FeZr3Ti3Cr2Fe4 cuboctahedra, faces with eight FeZr3Ti3Cr6 cuboctahedra, and faces with ten CrTi6Cr2Fe4 cuboctahedra. There are one shorter (2.40 Å) and one longer (2.51 Å) Cr–Cr bond lengths. There are one shorter (2.41 Å) and one longer (2.55 Å) Cr–Fe bond lengths. There are three inequivalent Fe sites. In the first Fe site, Fe is bonded to three Zr, three Ti, and six Cr atoms to form FeZr3Ti3Cr6 cuboctahedra that share corners with four CrTi6Cr2Fe4 cuboctahedra, corners with fourteen FeZr3Ti3Cr6 cuboctahedra, edges with six FeZr3Ti3Cr6 cuboctahedra, faces with four equivalent FeZr3Ti3Cr2Fe4 cuboctahedra, and faces with fourteen CrTi6Cr2Fe4 cuboctahedra. In the second Fe site, Fe is bonded to three Zr, three Ti, two Cr, and four Fe atoms to form distorted FeZr3Ti3Cr2Fe4 cuboctahedra that share corners with eight FeZr3Ti3Cr6 cuboctahedra, corners with ten CrTi6Cr2Fe4 cuboctahedra, edges with two equivalent FeZr3Ti3Cr2Fe4 cuboctahedra, edges with four equivalent CrZr3Ti3Cr4Fe2 cuboctahedra, faces with eight CrTi6Cr2Fe4 cuboctahedra, and faces with ten FeZr3Ti3Cr6 cuboctahedra. There are a spread of Fe–Fe bond distances ranging from 2.42–2.52 Å. In the third Fe site, Fe is bonded to three Zr, three Ti, two Cr, and four equivalent Fe atoms to form distorted FeZr3Ti3Cr2Fe4 cuboctahedra that share corners with six FeZr3Ti3Cr6 cuboctahedra, corners with twelve CrTi6Cr2Fe4 cuboctahedra, edges with six FeZr3Ti3Cr6 cuboctahedra, faces with eight equivalent FeZr3Ti3Cr2Fe4 cuboctahedra, and faces with ten CrTi6Cr2Fe4 cuboctahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-06-04. Materials Data on ZrTi(CrFe)2 by Materials Project. https://doi.org/10.17188/1733569

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗