Materials Data on Ni6SnSb by Materials Project

Abstract

Ni6SnSb is beta Cu3Ti-derived structured and crystallizes in the orthorhombic Pmm2 space group. The structure is three-dimensional. there are six inequivalent Ni sites. In the first Ni site, Ni is bonded to eight Ni, two equivalent Sn, and two equivalent Sb atoms to form NiNi8Sn2Sb2 cuboctahedra that share corners with four equivalent SbNi12 cuboctahedra, corners with fourteen NiNi8Sn2Sb2 cuboctahedra, edges with two equivalent SbNi12 cuboctahedra, edges with four equivalent SnNi12 cuboctahedra, edges with twelve NiNi8Sn2Sb2 cuboctahedra, faces with two equivalent SnNi12 cuboctahedra, faces with two equivalent SbNi12 cuboctahedra, and faces with sixteen NiNi8Sn2Sb2 cuboctahedra. There are a spread of Ni–Ni bond distances ranging from 2.56–2.73 Å. Both Ni–Sn bond lengths are 2.62 Å. There are one shorter (2.61 Å) and one longer (2.63 Å) Ni–Sb bond lengths. In the second Ni site, Ni is bonded to eight Ni, two equivalent Sn, and two equivalent Sb atoms to form NiNi8Sn2Sb2 cuboctahedra that share corners with four equivalent SbNi12 cuboctahedra, corners with fourteen NiNi8Sn2Sb2 cuboctahedra, edges with two equivalent SbNi12 cuboctahedra, edges with four equivalent SnNi12 cuboctahedra, edges with twelve NiNi8Sn2Sb2 cuboctahedra, faces with two equivalent SnNi12 cuboctahedra, faces with two equivalent SbNi12 cuboctahedra, and faces with sixteen NiNi8Sn2Sb2 cuboctahedra. There are a spread of Ni–Ni bond distances ranging from 2.56–2.73 Å. Both Ni–Sn bond lengths are 2.62 Å. There are one shorter (2.61 Å) and one longer (2.63 Å) Ni–Sb bond lengths. In the third Ni site, Ni is bonded to eight Ni, two equivalent Sn, and two equivalent Sb atoms to form NiNi8Sn2Sb2 cuboctahedra that share corners with four equivalent SnNi12 cuboctahedra, corners with fourteen NiNi8Sn2Sb2 cuboctahedra, edges with two equivalent SnNi12 cuboctahedra, edges with four equivalent SbNi12 cuboctahedra, edges with twelve NiNi8Sn2Sb2 cuboctahedra, faces with two equivalent SnNi12 cuboctahedra, faces with two equivalent SbNi12 cuboctahedra, and faces with sixteen NiNi8Sn2Sb2 cuboctahedra. There are a spread of Ni–Ni bond distances ranging from 2.56–2.70 Å. There are one shorter (2.62 Å) and one longer (2.65 Å) Ni–Sn bond lengths. Both Ni–Sb bond lengths are 2.61 Å. In the fourth Ni site, Ni is bonded to eight Ni, two equivalent Sn, and two equivalent Sb atoms to form NiNi8Sn2Sb2 cuboctahedra that share corners with four equivalent SnNi12 cuboctahedra, corners with fourteen NiNi8Sn2Sb2 cuboctahedra, edges with two equivalent SnNi12 cuboctahedra, edges with four equivalent SbNi12 cuboctahedra, edges with twelve NiNi8Sn2Sb2 cuboctahedra, faces with two equivalent SnNi12 cuboctahedra, faces with two equivalent SbNi12 cuboctahedra, and faces with sixteen NiNi8Sn2Sb2 cuboctahedra. There are a spread of Ni–Ni bond distances ranging from 2.56–2.70 Å. There are one shorter (2.62 Å) and one longer (2.65 Å) Ni–Sn bond lengths. Both Ni–Sb bond lengths are 2.61 Å. In the fifth Ni site, Ni is bonded to eight Ni, two equivalent Sn, and two equivalent Sb atoms to form NiNi8Sn2Sb2 cuboctahedra that share corners with eight equivalent SnNi12 cuboctahedra, corners with ten NiNi8Sn2Sb2 cuboctahedra, edges with eighteen NiNi8Sn2Sb2 cuboctahedra, faces with two equivalent SnNi12 cuboctahedra, faces with four equivalent SbNi12 cuboctahedra, and faces with fourteen NiNi8Sn2Sb2 cuboctahedra. Both Ni–Sn bond lengths are 2.65 Å. Both Ni–Sb bond lengths are 2.68 Å. In the sixth Ni site, Ni is bonded to eight Ni, two equivalent Sn, and two equivalent Sb atoms to form NiNi8Sn2Sb2 cuboctahedra that share corners with eight equivalent SbNi12 cuboctahedra, corners with ten NiNi8Sn2Sb2 cuboctahedra, edges with eighteen NiNi8Sn2Sb2 cuboctahedra, faces with two equivalent SbNi12 cuboctahedra, faces with four equivalent SnNi12 cuboctahedra, and faces with fourteen NiNi8Sn2Sb2 cuboctahedra. Both Ni–Sn bond lengths are 2.69 Å. Both Ni–Sb bond lengths are 2.65 Å. Sn is bonded to twelve Ni atoms to form SnNi12 cuboctahedra that share corners with two equivalent SnNi12 cuboctahedra, corners with sixteen NiNi8Sn2Sb2 cuboctahedra, edges with two equivalent SnNi12 cuboctahedra, edges with four equivalent SbNi12 cuboctahedra, edges with twelve NiNi8Sn2Sb2 cuboctahedra, faces with two equivalent SnNi12 cuboctahedra, faces with four equivalent SbNi12 cuboctahedra, and faces with fourteen NiNi8Sn2Sb2 cuboctahedra. Sb is bonded to twelve Ni atoms to form SbNi12 cuboctahedra that share corners with two equivalent SbNi12 cuboctahedra, corners with sixteen NiNi8Sn2Sb2 cuboctahedra, edges with two equivalent SbNi12 cuboctahedra, edges with four equivalent SnNi12 cuboctahedra, edges with twelve NiNi8Sn2Sb2 cuboctahedra, faces with two equivalent SbNi12 cuboctahedra, faces with four equivalent SnNi12 cuboctahedra, and faces with fourteen NiNi8Sn2Sb2 cuboctahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Ni6SnSb by Materials Project. https://doi.org/10.17188/1734289

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗