Materials Data on Na3V4(Bi10O21)2 by Materials Project

Abstract

Na3V4(Bi10O21)2 crystallizes in the monoclinic C2/m space group. The structure is three-dimensional. there are two inequivalent Na1+ sites. In the first Na1+ site, Na1+ is bonded in a distorted body-centered cubic geometry to eight O2- atoms. There are a spread of Na–O bond distances ranging from 2.48–2.86 Å. In the second Na1+ site, Na1+ is bonded to six O2- atoms to form NaO6 octahedra that share corners with two equivalent VO4 tetrahedra. There are two shorter (2.30 Å) and four longer (2.69 Å) Na–O bond lengths. There are two inequivalent V+4.75+ sites. In the first V+4.75+ site, V+4.75+ is bonded to four O2- atoms to form VO4 tetrahedra that share corners with two equivalent BiO6 octahedra. The corner-sharing octahedral tilt angles are 53°. There is three shorter (1.74 Å) and one longer (1.76 Å) V–O bond length. In the second V+4.75+ site, V+4.75+ is bonded to four O2- atoms to form VO4 tetrahedra that share a cornercorner with one NaO6 octahedra and corners with four equivalent BiO6 octahedra. The corner-sharing octahedra tilt angles range from 24–51°. There are a spread of V–O bond distances ranging from 1.71–1.77 Å. There are six inequivalent Bi+3.10+ sites. In the first Bi+3.10+ site, Bi+3.10+ is bonded to six O2- atoms to form distorted BiO6 pentagonal pyramids that share corners with two equivalent BiO6 octahedra and a cornercorner with one BiO4 trigonal pyramid. The corner-sharing octahedral tilt angles are 63°. There are a spread of Bi–O bond distances ranging from 2.12–2.66 Å. In the second Bi+3.10+ site, Bi+3.10+ is bonded to four O2- atoms to form distorted corner-sharing BiO4 trigonal pyramids. The corner-sharing octahedral tilt angles are 60°. There are a spread of Bi–O bond distances ranging from 2.13–2.39 Å. In the third Bi+3.10+ site, Bi+3.10+ is bonded in a 3-coordinate geometry to three O2- atoms. There are a spread of Bi–O bond distances ranging from 2.10–2.16 Å. In the fourth Bi+3.10+ site, Bi+3.10+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Bi–O bond distances ranging from 2.16–2.82 Å. In the fifth Bi+3.10+ site, Bi+3.10+ is bonded to six O2- atoms to form distorted BiO6 octahedra that share a cornercorner with one BiO6 pentagonal pyramid, corners with three VO4 tetrahedra, a cornercorner with one BiO4 trigonal pyramid, and an edgeedge with one BiO6 octahedra. There are a spread of Bi–O bond distances ranging from 2.17–2.76 Å. In the sixth Bi+3.10+ site, Bi+3.10+ is bonded in a 4-coordinate geometry to four O2- atoms. There are a spread of Bi–O bond distances ranging from 2.12–2.73 Å. There are fourteen inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted single-bond geometry to one V+4.75+ and two equivalent Bi+3.10+ atoms. In the second O2- site, O2- is bonded in a distorted trigonal planar geometry to three Bi+3.10+ atoms. In the third O2- site, O2- is bonded in a 3-coordinate geometry to three Bi+3.10+ atoms. In the fourth O2- site, O2- is bonded in a bent 150 degrees geometry to one Na1+ and one V+4.75+ atom. In the fifth O2- site, O2- is bonded in a distorted single-bond geometry to one V+4.75+ and two equivalent Bi+3.10+ atoms. In the sixth O2- site, O2- is bonded in a distorted single-bond geometry to one V+4.75+ and two Bi+3.10+ atoms. In the seventh O2- site, O2- is bonded in a distorted single-bond geometry to one V+4.75+ and two Bi+3.10+ atoms. In the eighth O2- site, O2- is bonded to two Na1+ and two Bi+3.10+ atoms to form distorted ONa2Bi2 tetrahedra that share corners with four ONa2Bi2 tetrahedra, a cornercorner with one ONaBi3 trigonal pyramid, an edgeedge with one ONa2Bi2 tetrahedra, and an edgeedge with one ONaBi3 trigonal pyramid. In the ninth O2- site, O2- is bonded in a 2-coordinate geometry to two Bi+3.10+ atoms. In the tenth O2- site, O2- is bonded in a distorted single-bond geometry to one V+4.75+ and two equivalent Bi+3.10+ atoms. In the eleventh O2- site, O2- is bonded to one Na1+ and three Bi+3.10+ atoms to form distorted ONaBi3 trigonal pyramids that share corners with two ONa2Bi2 tetrahedra, corners with two equivalent ONaBi3 trigonal pyramids, and edges with two ONa2Bi2 tetrahedra. In the twelfth O2- site, O2- is bonded in a trigonal planar geometry to three Bi+3.10+ atoms. In the thirteenth O2- site, O2- is bonded in a 4-coordinate geometry to one Na1+ and three Bi+3.10+ atoms. In the fourteenth O2- site, O2- is bonded to two equivalent Na1+ and two Bi+3.10+ atoms to form ONa2Bi2 tetrahedra that share corners with four equivalent ONa2Bi2 tetrahedra, corners with two equivalent ONaBi3 trigonal pyramids, an edgeedge with one ONa2Bi2 tetrahedra, and edges with two equivalent ONaBi3 trigonal pyramids.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Na3V4(Bi10O21)2 by Materials Project. https://doi.org/10.17188/1741492

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗