Materials Data on HfZn2Ga by Materials Project

Abstract

HfZn2Ga crystallizes in the trigonal R3m space group. The structure is three-dimensional. Hf is bonded to six equivalent Hf, three equivalent Zn, and three equivalent Ga atoms to form distorted HfHf6Zn3Ga3 cuboctahedra that share corners with six equivalent HfHf6Zn3Ga3 cuboctahedra, corners with six equivalent ZnZn9Ga3 cuboctahedra, edges with six equivalent HfHf6Zn3Ga3 cuboctahedra, edges with six equivalent GaHf3Zn3Ga6 cuboctahedra, edges with twelve ZnHf3Zn9 cuboctahedra, faces with six equivalent HfHf6Zn3Ga3 cuboctahedra, faces with six equivalent ZnHf3Zn9 cuboctahedra, and faces with six equivalent GaHf3Zn3Ga6 cuboctahedra. All Hf–Hf bond lengths are 2.99 Å. All Hf–Zn bond lengths are 2.96 Å. All Hf–Ga bond lengths are 2.96 Å. There are two inequivalent Zn sites. In the first Zn site, Zn is bonded to three equivalent Hf and nine Zn atoms to form distorted ZnHf3Zn9 cuboctahedra that share corners with six equivalent ZnHf3Zn9 cuboctahedra, corners with six equivalent GaHf3Zn3Ga6 cuboctahedra, edges with six equivalent HfHf6Zn3Ga3 cuboctahedra, edges with six equivalent GaHf3Zn3Ga6 cuboctahedra, edges with twelve ZnHf3Zn9 cuboctahedra, faces with six equivalent HfHf6Zn3Ga3 cuboctahedra, and faces with twelve ZnHf3Zn9 cuboctahedra. There are three shorter (2.74 Å) and six longer (2.99 Å) Zn–Zn bond lengths. In the second Zn site, Zn is bonded to nine Zn and three equivalent Ga atoms to form distorted ZnZn9Ga3 cuboctahedra that share corners with six equivalent HfHf6Zn3Ga3 cuboctahedra, corners with six equivalent ZnZn9Ga3 cuboctahedra, edges with six equivalent HfHf6Zn3Ga3 cuboctahedra, edges with six equivalent GaHf3Zn3Ga6 cuboctahedra, edges with twelve ZnHf3Zn9 cuboctahedra, faces with six equivalent GaHf3Zn3Ga6 cuboctahedra, and faces with twelve ZnHf3Zn9 cuboctahedra. All Zn–Zn bond lengths are 2.99 Å. All Zn–Ga bond lengths are 2.84 Å. Ga is bonded to three equivalent Hf, three equivalent Zn, and six equivalent Ga atoms to form distorted GaHf3Zn3Ga6 cuboctahedra that share corners with six equivalent ZnHf3Zn9 cuboctahedra, corners with six equivalent GaHf3Zn3Ga6 cuboctahedra, edges with six equivalent HfHf6Zn3Ga3 cuboctahedra, edges with six equivalent GaHf3Zn3Ga6 cuboctahedra, edges with twelve ZnHf3Zn9 cuboctahedra, faces with six equivalent HfHf6Zn3Ga3 cuboctahedra, faces with six equivalent ZnZn9Ga3 cuboctahedra, and faces with six equivalent GaHf3Zn3Ga6 cuboctahedra. All Ga–Ga bond lengths are 2.99 Å.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-04. Materials Data on HfZn2Ga by Materials Project. https://doi.org/10.17188/1741860

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗