Materials Data on Li2V3CuO8 by Materials Project

Abstract

Li2V3CuO8 is Hausmannite-derived structured and crystallizes in the triclinic P1 space group. The structure is three-dimensional. there are eight inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 54–67°. There are a spread of Li–O bond distances ranging from 1.99–2.01 Å. In the second Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 53–67°. There are a spread of Li–O bond distances ranging from 1.98–2.01 Å. In the third Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 53–66°. There are a spread of Li–O bond distances ranging from 1.98–2.01 Å. In the fourth Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 54–67°. There are a spread of Li–O bond distances ranging from 1.99–2.01 Å. In the fifth Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 53–67°. There are a spread of Li–O bond distances ranging from 1.99–2.01 Å. In the sixth Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 53–67°. There are a spread of Li–O bond distances ranging from 1.99–2.01 Å. In the seventh Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 53–66°. There are a spread of Li–O bond distances ranging from 1.99–2.01 Å. In the eighth Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with three CuO6 octahedra and corners with nine VO6 octahedra. The corner-sharing octahedra tilt angles range from 53–67°. There are a spread of Li–O bond distances ranging from 1.99–2.01 Å. There are twelve inequivalent V+4.33+ sites. In the first V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.89–2.06 Å. In the second V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.82–2.05 Å. In the third V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.83–2.06 Å. In the fourth V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.83–2.06 Å. In the fifth V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.82–2.06 Å. In the sixth V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.89–2.06 Å. In the seventh V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.89–2.06 Å. In the eighth V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.83–2.06 Å. In the ninth V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.83–2.05 Å. In the tenth V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.83–2.05 Å. In the eleventh V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.82–2.05 Å. In the twelfth V+4.33+ site, V+4.33+ is bonded to six O2- atoms to form VO6 octahedra that share corners with six LiO4 tetrahedra, edges with two CuO6 octahedra, and edges with four VO6 octahedra. There are a spread of V–O bond distances ranging from 1.89–2.06 Å. There are four inequivalent Cu1+ sites. In the first Cu1+ site, Cu1+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with six LiO4 tetrahedra and edges with six VO6 octahedra. There are a spread of Cu–O bond distances ranging from 2.00–2.23 Å. In the second Cu1+ site, Cu1+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with six LiO4 tetrahedra and edges with six VO6 octahedra. There are a spread of Cu–O bond distances ranging from 2.00–2.23 Å. In the third Cu1+ site, Cu1+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with six LiO4 tetrahedra and edges with six VO6 octahedra. There are a spread of Cu–O bond distances ranging from 2.00–2.24 Å. In the fourth Cu1+ site, Cu1+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with six LiO4 tetrahedra and edges with six VO6 octahedra. There are a spread of Cu–O bond distances ranging from 2.00–2.23 Å. There are thirty-two inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the second O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the third O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+ and three V+4.33+ atoms. In the fourth O2- site, O2- is bonded to one Li1+, two V+4.33+, and one Cu1+ atom to form distorted corner-sharing OLiV2Cu trigonal pyramids. In the fifth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the sixth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V+4.33+ atoms. In the seventh O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the eighth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the ninth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the tenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the eleventh O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V+4.33+ atoms. In the twelfth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the thirteenth O2- site, O2- is bonded to one Li1+, two V+4.33+, and one Cu1+ atom to form distorted corner-sharing OLiV2Cu trigonal pyramids. In the fourteenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+ and three V+4.33+ atoms. In the fifteenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the sixteenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the seventeenth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the eighteenth O2- site, O2- is bonded to one Li1+, two V+4.33+, and one Cu1+ atom to form distorted corner-sharing OLiV2Cu trigonal pyramids. In the nineteenth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V+4.33+ atoms. In the twentieth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the twenty-first O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the twenty-second O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V+4.33+ atoms. In the twenty-third O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the twenty-fourth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the twenty-fifth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the twenty-sixth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the twenty-seventh O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V+4.33+ atoms. In the twenty-eighth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom. In the twenty-ninth O2- site, O2- is bonded to one Li1+, two V+4.33+, and one Cu1+ atom to form distorted corner-sharing OLiV2Cu trigonal pyramids. In the thirtieth O2- site, O2- is bonded in a rectangular see-saw-like geometry to one Li1+ and three V+4.33+ atoms. In the thirty-first O2- site, O2- is bonded to one Li1+, two V+4.33+, and one Cu1+ atom to form distorted corner-sharing OLiV2Cu trigonal pyramids. In the thirty-second O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to one Li1+, two V+4.33+, and one Cu1+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-06-04. Materials Data on Li2V3CuO8 by Materials Project. https://doi.org/10.17188/1742479

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗