Materials Data on Dy3SOF5 by Materials Project

Abstract

Dy3SOF5 crystallizes in the monoclinic Pm space group. The structure is three-dimensional. there are six inequivalent Dy3+ sites. In the first Dy3+ site, Dy3+ is bonded in a 9-coordinate geometry to two equivalent S2-, two O2-, and five F1- atoms. Both Dy–S bond lengths are 2.88 Å. There are one shorter (2.31 Å) and one longer (2.35 Å) Dy–O bond lengths. There are a spread of Dy–F bond distances ranging from 2.33–2.43 Å. In the second Dy3+ site, Dy3+ is bonded in a 9-coordinate geometry to two equivalent S2-, one O2-, and six F1- atoms. Both Dy–S bond lengths are 2.87 Å. The Dy–O bond length is 2.24 Å. There are a spread of Dy–F bond distances ranging from 2.29–2.50 Å. In the third Dy3+ site, Dy3+ is bonded in a 9-coordinate geometry to two equivalent S2-, one O2-, and six F1- atoms. Both Dy–S bond lengths are 2.88 Å. The Dy–O bond length is 2.26 Å. There are a spread of Dy–F bond distances ranging from 2.28–2.45 Å. In the fourth Dy3+ site, Dy3+ is bonded in a 7-coordinate geometry to two equivalent S2-, two equivalent O2-, and five F1- atoms. Both Dy–S bond lengths are 3.00 Å. Both Dy–O bond lengths are 2.30 Å. There are a spread of Dy–F bond distances ranging from 2.30–2.45 Å. In the fifth Dy3+ site, Dy3+ is bonded in a 7-coordinate geometry to two equivalent S2- and seven F1- atoms. Both Dy–S bond lengths are 2.86 Å. There are a spread of Dy–F bond distances ranging from 2.30–2.39 Å. In the sixth Dy3+ site, Dy3+ is bonded in a 7-coordinate geometry to two equivalent S2-, two equivalent O2-, and five F1- atoms. Both Dy–S bond lengths are 2.99 Å. Both Dy–O bond lengths are 2.30 Å. There are a spread of Dy–F bond distances ranging from 2.29–2.53 Å. There are two inequivalent S2- sites. In the first S2- site, S2- is bonded in a 12-coordinate geometry to six Dy3+, two O2-, and ten F1- atoms. There are one shorter (3.26 Å) and one longer (3.29 Å) S–O bond lengths. There are a spread of S–F bond distances ranging from 3.08–3.25 Å. In the second S2- site, S2- is bonded in a 6-coordinate geometry to six Dy3+, four O2-, and eight F1- atoms. All S–O bond lengths are 3.09 Å. There are a spread of S–F bond distances ranging from 3.05–3.32 Å. There are two inequivalent O2- sites. In the first O2- site, O2- is bonded to four Dy3+ and three S2- atoms to form ODy4S3 tetrahedra that share corners with three equivalent ODy4S3 tetrahedra, corners with seven FDy4S3 tetrahedra, edges with two equivalent ODy4S3 tetrahedra, edges with four FDy4S3 tetrahedra, a faceface with one ODy4S3 tetrahedra, and faces with three FDy4S3 tetrahedra. In the second O2- site, O2- is bonded to four Dy3+ and three S2- atoms to form distorted ODy4S3 tetrahedra that share corners with three equivalent ODy4S3 tetrahedra, corners with seven FDy4S3 tetrahedra, edges with two equivalent ODy4S3 tetrahedra, edges with four FDy4S3 tetrahedra, a faceface with one ODy4S3 tetrahedra, and faces with three FDy4S3 tetrahedra. There are ten inequivalent F1- sites. In the first F1- site, F1- is bonded in a trigonal non-coplanar geometry to three Dy3+ and one S2- atom. In the second F1- site, F1- is bonded in a distorted trigonal non-coplanar geometry to three Dy3+ and one S2- atom. In the third F1- site, F1- is bonded in a distorted trigonal non-coplanar geometry to three Dy3+ and one S2- atom. In the fourth F1- site, F1- is bonded in a trigonal non-coplanar geometry to three Dy3+ and one S2- atom. In the fifth F1- site, F1- is bonded in a distorted trigonal non-coplanar geometry to three Dy3+ and one S2- atom. In the sixth F1- site, F1- is bonded in a trigonal non-coplanar geometry to three Dy3+ and one S2- atom. In the seventh F1- site, F1- is bonded to four Dy3+ and three S2- atoms to form distorted FDy4S3 tetrahedra that share corners with four FDy4S3 tetrahedra, corners with six ODy4S3 tetrahedra, edges with six FDy4S3 tetrahedra, faces with two ODy4S3 tetrahedra, and faces with two equivalent FDy4S3 tetrahedra. In the eighth F1- site, F1- is bonded to four Dy3+ and three S2- atoms to form distorted FDy4S3 tetrahedra that share corners with two equivalent ODy4S3 tetrahedra, corners with eight FDy4S3 tetrahedra, edges with two equivalent ODy4S3 tetrahedra, edges with four FDy4S3 tetrahedra, faces with two equivalent ODy4S3 tetrahedra, and faces with two FDy4S3 tetrahedra. In the ninth F1- site, F1- is bonded to four Dy3+ and three S2- atoms to form distorted FDy4S3 tetrahedra that share corners with two equivalent ODy4S3 tetrahedra, corners with eight FDy4S3 tetrahedra, edges with two equivalent ODy4S3 tetrahedra, edges with four FDy4S3 tetrahedra, faces with two equivalent ODy4S3 tetrahedra, and faces with two FDy4S3 tetrahedra. In the tenth F1- site, F1- is bonded to four Dy3+ and three S2- atoms to form distorted FDy4S3 tetrahedra that share corners with four ODy4S3 tetrahedra, corners with six FDy4S3 tetrahedra, edges with two equivalent FDy4S3 tetrahedra, edges with four ODy4S3 tetrahedra, and faces with four FDy4S3 tetrahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Dy3SOF5 by Materials Project. https://doi.org/10.17188/1745244

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗