Materials Data on B(HC)2 by Materials Project

View original source ↗Read source document ↗Export metadata ↓

Abstract

B(CH)2 crystallizes in the triclinic P-1 space group. The structure is zero-dimensional and consists of one B(CH)2 cluster. there are three inequivalent B3+ sites. In the first B3+ site, B3+ is bonded in a tetrahedral geometry to two C+2.50- and two H1+ atoms. Both B–C bond lengths are 1.52 Å. There is one shorter (1.24 Å) and one longer (1.26 Å) B–H bond length. In the second B3+ site, B3+ is bonded in a tetrahedral geometry to two C+2.50- and two H1+ atoms. Both B–C bond lengths are 1.52 Å. There is one shorter (1.24 Å) and one longer (1.26 Å) B–H bond length. In the third B3+ site, B3+ is bonded in a tetrahedral geometry to two C+2.50- and two H1+ atoms. Both B–C bond lengths are 1.52 Å. There is one shorter (1.24 Å) and one longer (1.26 Å) B–H bond length. There are six inequivalent C+2.50- sites. In the first C+2.50- site, C+2.50- is bonded in a distorted linear geometry to one B3+ and one C+2.50- atom. The C–C bond length is 1.25 Å. In the second C+2.50- site, C+2.50- is bonded in a distorted linear geometry to one B3+ and one C+2.50- atom. The C–C bond length is 1.26 Å. In the third C+2.50- site, C+2.50- is bonded in a distorted linear geometry to one B3+ and one C+2.50- atom. The C–C bond length is 1.25 Å. In the fourth C+2.50- site, C+2.50- is bonded in a distorted linear geometry to one B3+ and one C+2.50- atom. In the fifth C+2.50- site, C+2.50- is bonded in a distorted linear geometry to one B3+ and one C+2.50- atom. In the sixth C+2.50- site, C+2.50- is bonded in a distorted linear geometry to one B3+ and one C+2.50- atom. There are six inequivalent H1+ sites. In the first H1+ site, H1+ is bonded in a single-bond geometry to one B3+ atom. In the second H1+ site, H1+ is bonded in a single-bond geometry to one B3+ atom. In the third H1+ site, H1+ is bonded in a single-bond geometry to one B3+ atom. In the fourth H1+ site, H1+ is bonded in a single-bond geometry to one B3+ atom. In the fifth H1+ site, H1+ is bonded in a single-bond geometry to one B3+ atom. In the sixth H1+ site, H1+ is bonded in a single-bond geometry to one B3+ atom.

Explore related subjects

36 MATERIALS SCIENCEB(HC)2B-C-Hcrystal structure

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on B(HC)2 by Materials Project. https://doi.org/10.17188/1745609

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗