Materials Data on Eu2MgS4 by Materials Project

Abstract

MgEu2S4 crystallizes in the orthorhombic Pca2_1 space group. The structure is three-dimensional. there are two inequivalent Mg2+ sites. In the first Mg2+ site, Mg2+ is bonded to six S2- atoms to form MgS6 octahedra that share a cornercorner with one EuS6 octahedra, corners with two equivalent MgS6 octahedra, corners with four EuS7 pentagonal bipyramids, an edgeedge with one MgS6 octahedra, edges with four EuS6 octahedra, and edges with three EuS7 pentagonal bipyramids. The corner-sharing octahedra tilt angles range from 10–54°. There are a spread of Mg–S bond distances ranging from 2.51–2.92 Å. In the second Mg2+ site, Mg2+ is bonded to six S2- atoms to form MgS6 octahedra that share a cornercorner with one EuS6 octahedra, corners with two equivalent MgS6 octahedra, corners with four EuS7 pentagonal bipyramids, an edgeedge with one MgS6 octahedra, edges with four EuS6 octahedra, and edges with three EuS7 pentagonal bipyramids. The corner-sharing octahedra tilt angles range from 10–54°. There are a spread of Mg–S bond distances ranging from 2.50–2.82 Å. There are four inequivalent Eu3+ sites. In the first Eu3+ site, Eu3+ is bonded to six S2- atoms to form EuS6 octahedra that share a cornercorner with one MgS6 octahedra, corners with two equivalent EuS6 octahedra, corners with four EuS7 pentagonal bipyramids, an edgeedge with one EuS6 octahedra, edges with four MgS6 octahedra, and edges with three EuS7 pentagonal bipyramids. The corner-sharing octahedra tilt angles range from 10–54°. There are a spread of Eu–S bond distances ranging from 2.74–2.83 Å. In the second Eu3+ site, Eu3+ is bonded to six S2- atoms to form EuS6 octahedra that share a cornercorner with one MgS6 octahedra, corners with two equivalent EuS6 octahedra, corners with four EuS7 pentagonal bipyramids, an edgeedge with one EuS6 octahedra, edges with four MgS6 octahedra, and edges with three EuS7 pentagonal bipyramids. The corner-sharing octahedra tilt angles range from 10–54°. There are a spread of Eu–S bond distances ranging from 2.76–2.83 Å. In the third Eu3+ site, Eu3+ is bonded to seven S2- atoms to form distorted EuS7 pentagonal bipyramids that share corners with four MgS6 octahedra, corners with four EuS6 octahedra, edges with three MgS6 octahedra, edges with three EuS6 octahedra, and faces with two equivalent EuS7 pentagonal bipyramids. The corner-sharing octahedra tilt angles range from 14–72°. There are a spread of Eu–S bond distances ranging from 2.82–3.08 Å. In the fourth Eu3+ site, Eu3+ is bonded to seven S2- atoms to form distorted EuS7 pentagonal bipyramids that share corners with four MgS6 octahedra, corners with four EuS6 octahedra, edges with three MgS6 octahedra, edges with three EuS6 octahedra, and faces with two equivalent EuS7 pentagonal bipyramids. The corner-sharing octahedra tilt angles range from 15–73°. There are a spread of Eu–S bond distances ranging from 2.81–3.08 Å. There are eight inequivalent S2- sites. In the first S2- site, S2- is bonded to two Mg2+ and three Eu3+ atoms to form distorted SEu3Mg2 square pyramids that share corners with two equivalent SEu3Mg2 square pyramids, corners with three equivalent SEu3Mg tetrahedra, edges with five SEu3Mg2 square pyramids, and edges with two equivalent SEu4Mg trigonal bipyramids. In the second S2- site, S2- is bonded in a 5-coordinate geometry to two Mg2+ and three Eu3+ atoms. In the third S2- site, S2- is bonded to one Mg2+ and three Eu3+ atoms to form distorted SEu3Mg tetrahedra that share corners with seven SEu3Mg2 square pyramids, corners with three equivalent SEu4Mg trigonal bipyramids, and edges with three SEu3Mg2 square pyramids. In the fourth S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to one Mg2+ and three Eu3+ atoms. In the fifth S2- site, S2- is bonded to two Mg2+ and three Eu3+ atoms to form SEu3Mg2 square pyramids that share corners with two equivalent SEu3Mg2 square pyramids, a cornercorner with one SEu3Mg tetrahedra, corners with four equivalent SEu4Mg trigonal bipyramids, edges with five SEu3Mg2 square pyramids, and an edgeedge with one SEu3Mg tetrahedra. In the sixth S2- site, S2- is bonded to two Mg2+ and three Eu3+ atoms to form SEu3Mg2 square pyramids that share corners with two equivalent SEu4Mg square pyramids, a cornercorner with one SEu3Mg tetrahedra, corners with two equivalent SEu4Mg trigonal bipyramids, edges with five SEu3Mg2 square pyramids, an edgeedge with one SEu3Mg tetrahedra, and an edgeedge with one SEu4Mg trigonal bipyramid. In the seventh S2- site, S2- is bonded to one Mg2+ and four Eu3+ atoms to form distorted SEu4Mg square pyramids that share corners with two equivalent SEu3Mg2 square pyramids, corners with two equivalent SEu3Mg tetrahedra, corners with two equivalent SEu4Mg trigonal bipyramids, edges with five SEu3Mg2 square pyramids, an edgeedge with one SEu3Mg tetrahedra, and an edgeedge with one SEu4Mg trigonal bipyramid. In the eighth S2- site, S2- is bonded to one Mg2+ and four Eu3+ atoms to form distorted SEu4Mg trigonal bipyramids that share corners with eight SEu3Mg2 square pyramids, corners with three equivalent SEu3Mg tetrahedra, and edges with four SEu3Mg2 square pyramids.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-06-05. Materials Data on Eu2MgS4 by Materials Project. https://doi.org/10.17188/1746967

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗