Materials Data on MnAl6Si4O19 by Materials Project

Abstract

MnAl6Si4O19 crystallizes in the monoclinic P2_1/m space group. The structure is three-dimensional. Mn4+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Mn–O bond distances ranging from 1.83–2.46 Å. There are four inequivalent Al3+ sites. In the first Al3+ site, Al3+ is bonded to four O2- atoms to form AlO4 tetrahedra that share corners with six AlO6 octahedra and corners with two equivalent SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 49–61°. There are a spread of Al–O bond distances ranging from 1.73–1.79 Å. In the second Al3+ site, Al3+ is bonded to four O2- atoms to form AlO4 tetrahedra that share corners with four AlO6 octahedra and corners with three equivalent SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 51–58°. There are a spread of Al–O bond distances ranging from 1.73–1.79 Å. In the third Al3+ site, Al3+ is bonded to six O2- atoms to form AlO6 octahedra that share corners with two AlO4 tetrahedra, corners with two SiO4 tetrahedra, a cornercorner with one SiO5 trigonal bipyramid, edges with two equivalent AlO6 octahedra, and an edgeedge with one SiO5 trigonal bipyramid. There are a spread of Al–O bond distances ranging from 1.84–2.02 Å. In the fourth Al3+ site, Al3+ is bonded to six O2- atoms to form AlO6 octahedra that share corners with three AlO4 tetrahedra, corners with four SiO4 tetrahedra, and edges with two equivalent AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.85–2.05 Å. There are four inequivalent Si4+ sites. In the first Si4+ site, Si4+ is bonded to five O2- atoms to form SiO5 trigonal bipyramids that share corners with two equivalent AlO6 octahedra, a cornercorner with one SiO4 tetrahedra, and edges with two equivalent AlO6 octahedra. The corner-sharing octahedral tilt angles are 49°. There are a spread of Si–O bond distances ranging from 1.67–1.89 Å. In the second Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with two equivalent AlO6 octahedra and a cornercorner with one SiO5 trigonal bipyramid. The corner-sharing octahedral tilt angles are 53°. There are a spread of Si–O bond distances ranging from 1.62–1.68 Å. In the third Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with six AlO6 octahedra and corners with two equivalent AlO4 tetrahedra. The corner-sharing octahedra tilt angles range from 47–55°. There are a spread of Si–O bond distances ranging from 1.61–1.65 Å. In the fourth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with four AlO6 octahedra and corners with three equivalent AlO4 tetrahedra. The corner-sharing octahedra tilt angles range from 50–59°. There are a spread of Si–O bond distances ranging from 1.61–1.66 Å. There are fifteen inequivalent O2- sites. In the first O2- site, O2- is bonded in a linear geometry to one Al3+ and one Si4+ atom. In the second O2- site, O2- is bonded in a 4-coordinate geometry to one Mn4+ and three Al3+ atoms. In the third O2- site, O2- is bonded in a 3-coordinate geometry to two equivalent Al3+ and one Si4+ atom. In the fourth O2- site, O2- is bonded in a distorted trigonal planar geometry to two equivalent Al3+ and one Si4+ atom. In the fifth O2- site, O2- is bonded in a distorted bent 150 degrees geometry to one Mn4+ and one Si4+ atom. In the sixth O2- site, O2- is bonded in a bent 120 degrees geometry to two Si4+ atoms. In the seventh O2- site, O2- is bonded in a trigonal planar geometry to three Al3+ atoms. In the eighth O2- site, O2- is bonded in a 3-coordinate geometry to two equivalent Al3+ and one Si4+ atom. In the ninth O2- site, O2- is bonded in a distorted trigonal planar geometry to two equivalent Al3+ and one Si4+ atom. In the tenth O2- site, O2- is bonded in a trigonal non-coplanar geometry to two equivalent Al3+ and one Si4+ atom. In the eleventh O2- site, O2- is bonded in a distorted trigonal planar geometry to three Al3+ atoms. In the twelfth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Mn4+, one Al3+, and one Si4+ atom. In the thirteenth O2- site, O2- is bonded in a trigonal planar geometry to two Al3+ and one Si4+ atom. In the fourteenth O2- site, O2- is bonded in a trigonal planar geometry to two Al3+ and one Si4+ atom. In the fifteenth O2- site, O2- is bonded in a trigonal planar geometry to one Mn4+, one Al3+, and one Si4+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-30. Materials Data on MnAl6Si4O19 by Materials Project. https://doi.org/10.17188/1754963

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗