Materials Data on Zr8Sc2O19 by Materials Project

Abstract

Sc2Zr8O19 is alpha bismuth trifluoride-derived structured and crystallizes in the monoclinic Pm space group. The structure is three-dimensional. there are two inequivalent Sc3+ sites. In the first Sc3+ site, Sc3+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Sc–O bond distances ranging from 2.01–2.24 Å. In the second Sc3+ site, Sc3+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Sc–O bond distances ranging from 2.05–2.37 Å. There are eight inequivalent Zr4+ sites. In the first Zr4+ site, Zr4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Zr–O bond distances ranging from 2.11–2.32 Å. In the second Zr4+ site, Zr4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Zr–O bond distances ranging from 2.16–2.32 Å. In the third Zr4+ site, Zr4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Zr–O bond distances ranging from 2.15–2.28 Å. In the fourth Zr4+ site, Zr4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Zr–O bond distances ranging from 2.18–2.27 Å. In the fifth Zr4+ site, Zr4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Zr–O bond distances ranging from 2.18–2.24 Å. In the sixth Zr4+ site, Zr4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Zr–O bond distances ranging from 2.13–2.26 Å. In the seventh Zr4+ site, Zr4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Zr–O bond distances ranging from 2.08–2.33 Å. In the eighth Zr4+ site, Zr4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Zr–O bond distances ranging from 2.14–2.30 Å. There are nineteen inequivalent O2- sites. In the first O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the second O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the third O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the fourth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the fifth O2- site, O2- is bonded to two equivalent Sc3+ and two equivalent Zr4+ atoms to form a mixture of corner and edge-sharing OZr2Sc2 tetrahedra. In the sixth O2- site, O2- is bonded to two equivalent Sc3+ and two equivalent Zr4+ atoms to form distorted OZr2Sc2 tetrahedra that share corners with fourteen OSc4 tetrahedra and edges with five OZr4 tetrahedra. In the seventh O2- site, O2- is bonded to four Sc3+ atoms to form a mixture of corner and edge-sharing OSc4 tetrahedra. In the eighth O2- site, O2- is bonded to two equivalent Sc3+ and two equivalent Zr4+ atoms to form a mixture of corner and edge-sharing OZr2Sc2 tetrahedra. In the ninth O2- site, O2- is bonded to two equivalent Sc3+ and two equivalent Zr4+ atoms to form distorted OZr2Sc2 tetrahedra that share corners with fourteen OSc4 tetrahedra and edges with five OZr2Sc2 tetrahedra. In the tenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the eleventh O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the twelfth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the thirteenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the fourteenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the fifteenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the sixteenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the seventeenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the eighteenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the nineteenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-09-03. Materials Data on Zr8Sc2O19 by Materials Project. https://doi.org/10.17188/1757098

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗