Materials Data on Ca5TiSn4(BO3)10 by Materials Project

Abstract

Ca5TiSn4(BO3)10 is Calcite-derived structured and crystallizes in the triclinic P-1 space group. The structure is three-dimensional. there are three inequivalent Ca2+ sites. In the first Ca2+ site, Ca2+ is bonded to six O2- atoms to form CaO6 octahedra that share a cornercorner with one TiO6 octahedra and corners with five SnO6 octahedra. The corner-sharing octahedra tilt angles range from 57–59°. There are a spread of Ca–O bond distances ranging from 2.39–2.47 Å. In the second Ca2+ site, Ca2+ is bonded to six O2- atoms to form CaO6 octahedra that share corners with six SnO6 octahedra. The corner-sharing octahedral tilt angles are 57°. There are five shorter (2.38 Å) and one longer (2.39 Å) Ca–O bond lengths. In the third Ca2+ site, Ca2+ is bonded to six O2- atoms to form CaO6 octahedra that share corners with two equivalent SnO6 octahedra and corners with four equivalent TiO6 octahedra. The corner-sharing octahedral tilt angles are 57°. There are two shorter (2.37 Å) and four longer (2.46 Å) Ca–O bond lengths. Ti4+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with six CaO6 octahedra. The corner-sharing octahedra tilt angles range from 57–59°. There is four shorter (1.99 Å) and two longer (2.00 Å) Ti–O bond length. There are five inequivalent B3+ sites. In the first B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. All B–O bond lengths are 1.39 Å. In the second B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. All B–O bond lengths are 1.39 Å. In the third B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. All B–O bond lengths are 1.39 Å. In the fourth B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. There is one shorter (1.38 Å) and two longer (1.39 Å) B–O bond length. In the fifth B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. All B–O bond lengths are 1.39 Å. There are two inequivalent Sn4+ sites. In the first Sn4+ site, Sn4+ is bonded to six O2- atoms to form SnO6 octahedra that share corners with six CaO6 octahedra. The corner-sharing octahedra tilt angles range from 57–58°. There are one shorter (2.08 Å) and five longer (2.09 Å) Sn–O bond lengths. In the second Sn4+ site, Sn4+ is bonded to six O2- atoms to form SnO6 octahedra that share corners with six CaO6 octahedra. The corner-sharing octahedral tilt angles are 57°. All Sn–O bond lengths are 2.09 Å. There are fifteen inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the second O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the third O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the fourth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the fifth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one Ti4+, and one B3+ atom. In the sixth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the seventh O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the eighth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the ninth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the tenth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one Ti4+, and one B3+ atom. In the eleventh O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the twelfth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the thirteenth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the fourteenth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one B3+, and one Sn4+ atom. In the fifteenth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ca2+, one Ti4+, and one B3+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-09-03. Materials Data on Ca5TiSn4(BO3)10 by Materials Project. https://doi.org/10.17188/1757503

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗