Materials Data on Ca4CoSi8(NiO8)3 by Materials Project

Abstract

Ca4CoSi8(NiO8)3 is Esseneite-derived structured and crystallizes in the monoclinic P2 space group. The structure is three-dimensional. there are four inequivalent Ca2+ sites. In the first Ca2+ site, Ca2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.34–2.77 Å. In the second Ca2+ site, Ca2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.34–2.77 Å. In the third Ca2+ site, Ca2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.34–2.77 Å. In the fourth Ca2+ site, Ca2+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Ca–O bond distances ranging from 2.34–2.77 Å. Co2+ is bonded to six O2- atoms to form CoO6 octahedra that share corners with six SiO4 tetrahedra and edges with two equivalent NiO6 octahedra. There are a spread of Co–O bond distances ranging from 2.08–2.16 Å. There are three inequivalent Ni2+ sites. In the first Ni2+ site, Ni2+ is bonded to six O2- atoms to form NiO6 octahedra that share corners with six SiO4 tetrahedra and edges with two equivalent NiO6 octahedra. There are four shorter (2.08 Å) and two longer (2.14 Å) Ni–O bond lengths. In the second Ni2+ site, Ni2+ is bonded to six O2- atoms to form NiO6 octahedra that share corners with six SiO4 tetrahedra and edges with two equivalent CoO6 octahedra. There are four shorter (2.08 Å) and two longer (2.14 Å) Ni–O bond lengths. In the third Ni2+ site, Ni2+ is bonded to six O2- atoms to form NiO6 octahedra that share corners with six SiO4 tetrahedra and edges with two equivalent NiO6 octahedra. There are four shorter (2.08 Å) and two longer (2.14 Å) Ni–O bond lengths. There are four inequivalent Si4+ sites. In the first Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share a cornercorner with one CoO6 octahedra, corners with two NiO6 octahedra, and corners with two equivalent SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 35–58°. There are a spread of Si–O bond distances ranging from 1.61–1.70 Å. In the second Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share a cornercorner with one CoO6 octahedra, corners with two NiO6 octahedra, and corners with two equivalent SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 35–58°. There are a spread of Si–O bond distances ranging from 1.60–1.70 Å. In the third Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share corners with three NiO6 octahedra and corners with two equivalent SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 35–58°. There are a spread of Si–O bond distances ranging from 1.61–1.70 Å. In the fourth Si4+ site, Si4+ is bonded to four O2- atoms to form SiO4 tetrahedra that share a cornercorner with one CoO6 octahedra, corners with two NiO6 octahedra, and corners with two equivalent SiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 35–59°. There are a spread of Si–O bond distances ranging from 1.60–1.70 Å. There are twelve inequivalent O2- sites. In the first O2- site, O2- is bonded in a 4-coordinate geometry to one Ca2+, two Ni2+, and one Si4+ atom. In the second O2- site, O2- is bonded in a 4-coordinate geometry to one Ca2+, one Co2+, one Ni2+, and one Si4+ atom. In the third O2- site, O2- is bonded in a 4-coordinate geometry to one Ca2+, two Ni2+, and one Si4+ atom. In the fourth O2- site, O2- is bonded in a 4-coordinate geometry to one Ca2+, one Co2+, one Ni2+, and one Si4+ atom. In the fifth O2- site, O2- is bonded in a 2-coordinate geometry to two Ca2+ and two Si4+ atoms. In the sixth O2- site, O2- is bonded in a 2-coordinate geometry to two Ca2+ and two Si4+ atoms. In the seventh O2- site, O2- is bonded in a 2-coordinate geometry to two Ca2+ and two Si4+ atoms. In the eighth O2- site, O2- is bonded in a 2-coordinate geometry to two Ca2+ and two Si4+ atoms. In the ninth O2- site, O2- is bonded in a distorted T-shaped geometry to one Ca2+, one Co2+, and one Si4+ atom. In the tenth O2- site, O2- is bonded in a distorted T-shaped geometry to one Ca2+, one Ni2+, and one Si4+ atom. In the eleventh O2- site, O2- is bonded in a distorted T-shaped geometry to one Ca2+, one Ni2+, and one Si4+ atom. In the twelfth O2- site, O2- is bonded in a distorted T-shaped geometry to one Ca2+, one Ni2+, and one Si4+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-09-03. Materials Data on Ca4CoSi8(NiO8)3 by Materials Project. https://doi.org/10.17188/1758239

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗