Interface creation on a mixed-terminated perovskite surface

Abstract

In the field of complex oxide heterostructures, understanding of the initial substrate surface can be critical to fundamental studies regarding the development of emergent properties at the film–substrate interface. For this reason, a considerable amount of effort has gone into the development of techniques to achieve surfaces with single termination for a variety of perovskite single crystals. However, a decisive understanding of how an interface is created when epitaxial growth occurs on a mixed terminated surface remains lacking. Employing in situ synchrotron X-ray scattering during thin film growth by molecular beam epitaxy, we investigate the initial stages of growth on (LaAlO 3 )(Sr 2 AlTaO 6 ) (001) substrates with mixed termination. Using LaNiO 3 as a model system, we find that the surface layers of the substrate restructure during deposition such that while a NiO 2 monolayer is weakly bound, a LaO monolayer bonds strongly, effectively incorporating with (Al, Ta)O 2 from the surface and forming a La(Al, Ta)O 3 ultrathin film. <!--/abstract content--><!--fulltext content--> With regard to the synthesis of high-quality complex oxide heterostructures, it is important that the substrate meet an array of criteria related to the crystal structure, lattice parameter, thermodynamic properties, electrical and optical properties, and so on. In particular, the surface of the substrate should be atomically smooth and exhibit the step-terrace structure ideal for epitaxial thin film growth. Perovskite oxides with the formula ABO 3 have two possible (001) surfaces: AO (A-site termination) and BO 2 (B-site termination). The ability to consistently achieve one of these surface terminations on SrTiO 3 , i.e., TiO 2 , has helped SrTiO 3 become the predominant oxide in the field.