Crystalline Mesoporous Complex Oxides: Porosity-Controlled Electromagnetic Response

Abstract

A colloidal--amphiphile--templated growth is developed to synthesize mesoporous complex oxides with highly crystalline frameworks. Organosilane-containing colloidal templates can convert into thermally stable silica that prevents the overgrowth of crystalline grains and the collapse of the mesoporosity. Using ilmenite CoTiO 3 as an example, the high crystallinity and the extraordinary thermal stability of its mesoporosity are demonstrated at 800 °C for 48 h under air. This synthetic approach is general and applicable to a series of complex oxides that are not reported with mesoporosity and high crystallinity, such as NiTiO 3 , FeTiO 3 , ZnTiO 3 , Co 2 TiO 4 , Zn 2 TiO 4 , MgTi 2 O 5 , and FeTi 2 O 5 . Those novel materials make it possible to build up correlations between mesoscale porosity and surface-sensitive physicochemical properties, e.g., electromagnetic response. For mesoporous CoTiO 3 , there is a 3 K increase of its antiferromagnetic ordering temperature, compared with that of nonporous one. Lastly, this finding provides a general guideline to design mesoporous complex oxides that allow exploring their unique properties different from bulk materials.