High spatial resolution thermal conductivity mapping of SiC/SiC composites

Abstract

Herein, silicon carbide (SiC) ceramic matrix composites are being investigated as a new generation of fuel cladding materials due to its higher accident tolerance compared to Zircaloy. Characterization of the thermal conductivity of SiC constituents and their interfaces and interphases in SiC/SiC composites is needed as inputs to models of cladding performance. We used time-domain thermoreflectance (TDTR) to map the thermal conductivity with a spatial resolution of 2 µm. The SiC/SiC composite is comprised of Hi-Nicalon Type S fibers in a matrix made by chemical vapor infiltration (CVI matrix). The interphase material is a pyrolytic carbon/SiC multilayer. We report thermal conductivity maps of the SiC fiber and SiC matrix at temperatures of 25 °C, 90 °C, 164 °C, and 250 °C. The fiber has a uniform and isotropic thermal conductivity of 22 W m -1 K -1 at 25 °C; the thermal conductivity of fiber is approximately independent of temperature. The matrix thermal conductivity is not uniform and varies from 50 to 120 W m -1 K -1 at 25 °C; the thermal conductivity of the matrix scales approximately with the inverse of the square root of temperature, i.e., ∝ 1/T 1/2 . The thermal conductivity of the interphase at room temperature is 6 W m -1 K -1 . The calculated spatially averaged thermal conductivity of this SiC/SiC composite at 1000°C is 29 W m -1 K -1 .

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Pek, Ella Kartika, Brethauer, John, Cahill, David G.. 2020-09-11. High spatial resolution thermal conductivity mapping of SiC/SiC composites. https://doi.org/10.1016/j.jnucmat.2020.152519

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Evaluating transient fission gas release in high burnup light water reactor fuel during loss of coolant accident conditions via new capabilities

In this work, the role of transient fission gas release (tFGR) in the cladding burst behavior of high burnup fuel during a loss-of-coolant accident (LOCA) in commercial light water reactors was further investigated via the use of a new apparatus. During the LOCA-related temperature ramps of high burnup fuel, the release of fission gases exceeds the steady-state release observed under normal operating conditions. An enhancement was made to the Oak Ridge National Laboratory Severe Accident Test Station (SATS) to probe the various factors influencing tFGR. Experiments were performed on commercially irradiated, zirconium-clad uranium dioxide fuel, and this paper details the design of the experimental setup, the initial test results, and the subsequent post-test analyses. Notably, the first test on high burnup fuel demonstrated a LOCA-relevant tFGR of 5.3% from an unpressurized fuel segment. The ultimate tFGR was 10.7% for beyond LOCA conditions. A follow-up test on similar fuel revealed a tFGR of 12.6% under comparable conditions. Microstructural analysis and an analysis of the released gas provide some insight regarding the source of tFGR in the fuel. Finally, a grain boundary bubble model may aid in the interpretation of the results and offer a guide for future work.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Characterization of ceramic fuel powder packing fractions to support INFLUX

Triply periodic minimal surface (TPMS)-based structures show marked potential in novel nuclear reactor fuel designs, as their high surface area-to-volume ratio increases the efficiency of heat transfer out of the fuel, enabling safer, more innovative reactor designs. This milestone report addresses the role of dUO 2 powder processing route on the fill behavior of TPMS-based cladding shells to understand and advance the feasibility of manufacturing TPMS-based nuclear fuel forms. dUO 2 powder was processed through either a dry granulation route, varying consolidation pressure, or through milling, varying milling time, milling method and milled size distribution. The lowest tapped bulk densities (TBD), but best powder flowabilities, were obtained when testing unprocessed dUO 2 powder which was prone to self-agglomeration and formed low-density spheroids. The highest TBD and lowest flowabilities were obtained when using powder produced by hammer-milling dUO 2 powder to pass through a 200-mesh sieve, which led to particles with angular morphologies. Powder produced by dry granulation exhibited TBD that varied according to the consolidation pressure used to form the initial pellets and exhibited improved flowabilities when compared to hammer-milled material. Because of the large span of granule sizes formed as well as the irregular shape associated with the granules, a packing fraction of 0.69 was achieved, exceeding the analytical solution for random close packing of mono-sized spheres. TPMS polymer shells were loaded with unprocessed, granulated, and hammer-milled dUO 2 powders, and their qualitative packing behaviors were analyzed using x-ray computed tomography (xCT). TBDs calculated after loading TPMS polymer shells were 10-20% lower when compared to tapped bulk density measurements taken in a glass graduated cylinder, indicating a non-trivial impact on the tapped bulk density of either the TPMS channel size, TPMS channel surface material, powder cohesiveness, or a combination of the two parameters. A metallic zircaloy-4 TPMS shell will be loaded with hammer-milled dUO 2 powder upon receipt of the shell from Oak Ridge National Laboratory (ORNL) and shipped to Idaho National Labs (INL) for subsequent hot isostatic pressing (HIP) densification experiments.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗