Liquid state properties and solidification features of the pseudo binary BaS-La 2 S 3

Abstract

The high temperature thermodynamic properties of chalcogenides materials based on BaS remain elusive. Herein the pseudo binary BaS-La 2 S 3 is investigated above 1573 K. The liquid properties of BaS-La 2 S 3 are measured by means of high resolution in-situ visualization coupled with thermal arrest measurements in a thermal imaging furnace. This enables to report the first observation of such melts in a container-less setting. The melting points of BaS and La 2 S 3 are revisited at 2454 K and 2004 K respectively. La 2 S 3 demonstrates a high stability in its liquid state, in strike difference with the sublimation observed for BaS. BaS is however partially stabilized with the addition of few percents of La 2 S 3 . The remarkable chemical and thermal stability of La 2 S 3 -rich samples contrasts with the partial decomposition and high vapor pressure observed for BaS-rich samples. Observations and analysis of the solidified samples suggest three different solid solutions. Solid and liquid densities are investigated along the different compositions, supporting a first estimate of the volumetric thermal expansion coefficient for La 2 S 3 .