A novel solid oxide electrolytic cell with reduced endothermic load for CO 2 electrolysis using (La 0.80 Sr 0.20 ) 0.95 MnO 3-δ cathode

Abstract

CO 2 conversion to CO via solid oxide electrolysis provides a potentially efficient method for converting CO 2 into an industrially relevant product. A solid oxide electrolysis cell with (La 0.80 Sr 0.20 ) 0.95 MnO 3-δ (LSM) as the CO 2 reduction cathode, yttrium stabilized zirconia (YSZ) as electrolyte, and nickel as the H 2 oxidation anode was operated 800 °C and 850 °C. Thermogravimetric analysis of the LSM material showed no catalyst oxidation at operating temperatures allowing for CO 2 electrolysis without reducing safe gas. In addition, no cathode material mass gain was observed in the presence of CO suggesting little to no carbon deposition occurred above 750 °C. The formation rates of CO for the cell reached 1.15 mL∙min-1∙ cm -2 for an applied current of 150 mA∙cm -2 achieving a faradaic efficiency of 100 %. Furthermore, the cell displayed good stability in the short-term CO 2 electrolysis test with a nominal voltage drop of 4 mV h -1 for 10 h at 850°C. This study shows the feasibility of operating a solid oxide CO 2 electrolysis cell for CO production with H 2 at the anode to reduce endothermic process load.