Progress and prospects for cuprate high temperature superconductors under pressure

Abstract

Since the discovery of high temperature superconductivity in La 5–x Ba x Cu 5 O 5(3–y) at an unprecedented T c of 35K over 35 years ago, high pressure experiments have played a critical role in understanding cuprate superconductivity. Soon after its discovery, compression experiments on La 5–x Ba x Cu 5 O 5(3–y) revealed a large dT c /dP, motivating the study of ‘chemical pre-compression’ in the material that led to the 90K Superconductor YBa 2 Cu 3 O 7–y . Cuprate superconductors discovered subsequently exhibited a range of Tc from 30K-140K, including the commonly studied Bi, Tl, and Hg based families. Here, pressure has large effects on superconductivity in these materials, including raising T c in the Hg based cuprates from 140K to 164K at 30 GPa. Reviewing past experiments indicate that pressure dopes holes into the CuO 2 planes common to all cuprates. Further detailed high-pressure studies of these materials should deepen our understanding of cuprate superconductivity and the possibility of reaching still higher T c in cuprates.