Material Characterization for Large Scale Additive Manufacturing (AM)

Abstract

The objective of this project was to enable prediction of residual stresses and warpage for extrusion deposition additive manufacturing (EDAM) fabricated carbon fiber thermoplastic matrix parts with three different materials systems produced by Techmer. The materials selected include Polyphenylene sulfide reinforced with 50% by weight of carbon fiber (CF-PPS), Polyethersulfone reinforced with 25% by weight of carbon fiber (CF-PESU), Polysulfone reinforced with 25% by weight of carbon fiber (CF-PSU). ADDITIVE3D © , a physics-based simulation workflow for EDAM, provided the simulation capabilities required for this project. Simulation predictions were validated against measurements carried out during and after the printing process carried out in the CAMRI and LSAM systems . Predictions for temperature, degree of crystallinity and deformation were carried out for the three material systems and two different geometries. Predictions for temperature were correlated very well with the experimental measurements for the two geometries printed using the three-material systems. The crystallinity level was verified for CF-PPS. The predictions for part deformation were in good agreement with the experimental measurements. In the best-case, predictions were within 8% of the maximum displacement observed in the 3-direction whereas predictions were within 14% for the worst-case. The adoption of this technology in commercial large-scale EDAM production processes would dramatically reduce the costs associated with producing articles by that process. Many thousands of dollars in materials, energy, and machine time could be saved by utilizing this simulation technology to develop articles rather than iterative printings to arrive at the optimal or correct design. The avoidance of a single failed print has the possibility of saving tens of thousands of dollars involved in the cost of material, machine and operators’ time.