Thermal Neutron Scattering Cross Sections for Graphitic Amorphous Carbon

Abstract

Carbon materials are commonly found in both nuclear reactors and experimental systems. Various carbon structures occur in nuclear applications ranging from crystalline and nuclear graphite to the amorphous carbon seen in next-generation advanced reactor designs. Amorphous carbon is based on a randomized graphite-like structure and offers the unique ability to disperse impurities throughout the bulk composition. A graphite-like amorphous carbon system was modeled using the classical molecular dynamics (MD) code LAMMPS (Large-scale Atomic/Molecular Massively Parallel Simulator). An improved version of the temperature-dependent Adaptive Intermolecular Reactive Empirical Bond Order (AIREBO) potential was used to model the carbon-carbon atomic interactions for the temperature at 300 K along with densities 1.60, 1.70, 1.85, and 2.23 g/cm 3 . From the normalized velocity autocorrelation function (VACF), the phonon density of state (DOS) was then calculated as the Fourier transform of the normalized VACF. This DOS was then used as the primary input for the evaluation of the thermal scattering law (TSL, i.e. S(α,β)) and associated neutron thermal scattering cross sections. The TSL was analyzed using the Full Law Analysis Scattering System Hub (FLASSH). The amorphous structure results in shifts of the phonon DOS to lower energy modes than typically displayed for ideal crystalline graphite. This impact on the DOS is directly reflected in the TSL. Furthermore, the typical features and the optical graphitic peak at 0.25 eV for the ideal graphite DOS disappear for graphite-like amorphous carbon, which shows good agreement with the expected structure.